Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Secondary orientation effects on the low cycle fatigue behaviors of rectangular‐sectional Ni‐based single crystal superalloys at medium and high temperatures

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effects of secondary orientation and temperature on the fretting fatigue behaviors of Ni-based single crystal superalloys

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Effects of secondary orientation on fatigue crack initiation in a single crystal superalloy

Effects of Secondary Orientation on Crack Closure Behavior of Nickel-Based Single Crystal Superalloys

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

Deformation mechanisms of low cycle fatigue of a fourth generation Ni-based single crystal superalloy

Effect of misorientation on the fatigue life of nickel-base single crystal superalloy DD5 at 980 °C

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

In-situ Observations of the Effects of Orientation and Carbide on Low Cycle Fatigue Crack Propagation in a Single Crystal Superalloy

High temperature in-situ SEM observation and crystal plasticity simulation on fretting fatigue of Ni-based single crystal superalloys

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

Life Assessment of Anisotropic Low Cycle Fatigue of Nickel-Base Single Crystal Superalloy

Effects of secondary orientations on long fatigue crack growth in a single crystal superalloy

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Effect of Local Recrystallized Grains on the Low Cycle Fatigue Behavior of a Nickel-Based Single Crystal Superalloy

In-Situ Sem Observation and Crystal Plasticity Finite Element Simulation of Fretting Fatigue Crack Formation in Ni-Base Single-Crystal Superalloys

Effects of Temperature and Secondary Orientations on the Deformation Behavior of Single-Crystal Superalloys