Abstract:The mechanical properties of nickel-based single crystal superalloys deteriorate with increasing misorientation, thus the finished product rate of the casting of single crystal turbine airfoils may be reduced due to the formation of grain boundaries especially when the misorientation angle exceeds to some extent. To this day, evolution of the microstructures at the grain boundaries with misorientation and the relationship between the microstructures and the mechanical properties are still unclear. In this work a detailed characterization of the misorientation related microstructure at the grain boundary in DD6 single crystal superalloy has been carried out using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques; the elemental distribution at the grain boundaries has been analyzed by energy dispersive (EDS) X-ray mapping; and the effect of precipitation of μ phases at the grain boundary on the mechanical property has been evaluated by finite element calculation. It is shown that the proportion of γ phase at the grain boundaries decreases, while the proportion of γ′ phase at the grain boundaries increases with increasing misorientation; the μ phase is precipitated at the grain boundaries when the misorientation angle exceeds about 10° and thus it could lead to a dramatic deterioration of the mechanical properties, as well as that the enrichment of Re and W gradually disappears as the misorientation angle increases. All these factors may result in the degradation of the mechanical properties at the grain boundaries as the misorientation increases. Furthermore, the finite element calculation confirms that precipitation of μ phases at the grain boundary is responsible for the significant deterioration of the mechanical properties when the misorientation exceeds about 10°. This work provides a physical imaging of the microstructure for understanding the relationship between the mechanical properties and the misorientation of the grain boundaries in the single crystal superalloy. Based on our study we hope that we can offer some scientific basis for further improvement of the nickel-based single crystal superalloys.

Effect of misorientation on the fatigue life of nickel-base single crystal superalloy DD5 at 980 °C

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

Crystal Orientation Effect on Fretting Fatigue Induced Geometrically Necessary Dislocation Distribution in Ni-based Single-Crystal Superalloys

In-Situ Sem Observation and Crystal Plasticity Finite Element Simulation of Fretting Fatigue Crack Formation in Ni-Base Single-Crystal Superalloys

Misorientation Related Microstructure at the Grain Boundary in A Nickel-Based Single Crystal Superalloy

High temperature in-situ SEM observation and crystal plasticity simulation on fretting fatigue of Ni-based single crystal superalloys

Secondary orientation effects on the low cycle fatigue behaviors of rectangular‐sectional Ni‐based single crystal superalloys at medium and high temperatures

In-situ Observations of the Effects of Orientation and Carbide on Low Cycle Fatigue Crack Propagation in a Single Crystal Superalloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Anisotropic Thermomechanical Fatigue of a Nickel-Base Single-Crystal Superalloy Part I: Effects of Crystal Orientations and Damage Mechanisms

Effects of secondary orientation and temperature on the fretting fatigue behaviors of Ni-based single crystal superalloys

Life Assessment of Anisotropic Low Cycle Fatigue of Nickel-Base Single Crystal Superalloy

Near-threshold fatigue crack propagation in a Ni-based single crystal superalloy affected by crystallographic anisotropy

Effects of secondary orientation on fatigue crack initiation in a single crystal superalloy

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Fretting Fatigue Experiment and Polycrystal Plasticity Simulation in Ni-based Superalloy at Room Temperature and 650 °C

A Low Cycle Fatigue Life Prediction Model Of Single Crystal Nickel-Based Superalloys Using Critical Plane Approach Combined With Crystallographic Slip Theory

High-cycle Fatigue Failure Behavior of Nickel-Based Single Crystal Alloys with Different Deviation Angles in a High-Temperature Environment