Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

High-cycle Fatigue Failure Behavior of Nickel-Based Single Crystal Alloys with Different Deviation Angles in a High-Temperature Environment

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

In-situ SEM study on fatigue crack behavior of a nickel-based single crystal alloy at 950 °C and 1050 °C

Evolution of fatigue mechanical properties and micro defects in nickel-based single crystal superalloys: A molecular dynamics research

Thermo-Mechanical Fatigue Behavior of A Single Crystal Nickel-Based Superalloy

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Temperature effect on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

Life Assessment of Anisotropic Low Cycle Fatigue of Nickel-Base Single Crystal Superalloy

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

Deformation behavior and crack mechanism of a first generation single-crystal Ni-based superalloys under thermomechanical fatigue loading

Investigation of low-cycle fatigue characteristics of nickel-based heat-resistant single-crystal alloy

Orientation and temperature dependence of yielding and deformation behavior of a nickel-base single crystal superalloy

Anisotropic Thermomechanical Fatigue of a Nickel-Base Single-Crystal Superalloy Part I: Effects of Crystal Orientations and Damage Mechanisms

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

Lattice Rotation and Deformation Mechanisms under Tensile Loading in a Single-Crystal Superalloy with [001] Misorientation

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Fretting fatigue damage mechanism of Nickel-based single crystal superalloys at high temperature