Phase Interface-Induced Dwell Fatigue Cracks in Titanium Alloy with Lamellar Microstructure

Zhichun Zhou,Binbin Jiang,Jianke Qiu,Linglei Zhang,Jiafeng Lei,Rui Yang,Kui Du

DOI: https://doi.org/10.1007/s40843-023-2641-7

2023-01-01

Abstract:Titanium alloys have been widely used in aerospace, energy, chemical and medical industries, especially in aero-engines, attributed to their high specific strength, good fatigue performance and excellent corrosion resistance. However, aero-engine components are usually subjected to dwell fatigue during aircraft operation, which significantly deteriorates the fatigue life and easily threatens aviation safety. Thus it is essential to understand the dwell fatigue behavior of titanium alloys. In this work, the formation mechanism of cracks in titanium alloys with lamellar microstructure has been investigated on low-cycle dwell fatigue. The deformation of α and β laths does not match in colonies, so the dislocation slip of α-Ti gives rise to extensive residual dislocation pile-up at α/β interfaces. The local tensile stress generated by residual dislocations is high and thus promotes the formation and coalescence of cavities in colonies, resulting in dwell fatigue cracks. These results provide insights on the formation of cracks in titanium alloy with lamellar microstructure under dwell fatigue, and they also give implications on the cracking of materials with lamellar microstructures in general.