Abstract:In ITER, the helium (He) impurity produced by the deuterium-tritium reaction will bombard the tungsten (W) divertor armor at the strike points. Consequently, strong interaction occurs therein that both impact the performance of the plasmas and the lifetime of the divertor. Despite an ever-increasing understanding of this interaction, some experimental phenomena remain mysterious, especially the formation of orientation-dependent surface morphologies. Here, we combine multiscale experimental characterization and theoretical models to shed new light on this problem. After low-energy He plasma exposure in a linear plasma generator, the polycrystalline W surface developed various morphologies. Through electron backscatter diffraction analysis, we found that the {111} grains developed cube-corner structures, the {110} grains developed ripple structures, whereas the {100} grains remained smooth. Then, electron-transparent lamellae were extracted from such grains to observe the subsurface He bubbles by transmission electron microscopy. The volume density, size distribution, and depth range of the He bubbles weakly depend on the crystallographic orientation, suggesting that the migration of W atoms causes the morphology variety. Accordingly, we proposed a two-stage formation mechanism. First, W atoms generated by over-pressurized He bubbles glide on the slip plane and in the slip direction to reach the surface, forming characteristic patterns that are enclosed by the slip traces. Second, morphological instability drives the evolution of the surface patterns, in which the initial surface structure and surface self-diffusion kinetics mediate. The proposed mechanism has been incorporated into a topographical instability model to enable asemi-quantitative analysis. The obtained new insights are valuable to the impurity control of the core plasmas and the lifetime analysis of the divertor for ITER.

Enhanced Modification of Tungsten Surface by Nanostructure Formation During High Flux Deuterium Plasma Exposure

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Nanostructures and pinholes on W surfaces exposed to high flux D plasma at high temperatures

Surface Diversifying and Deuterium Retention Characteristics of Doped Graphite with SiC Coating Exposed to Plasma Discharges in EAST Tokamak

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Formation of Orientation-Dependent Surface Morphologies on Tungsten after Low Energy Helium Plasma Exposure: Multiscale Characterization and New Insights

Modelling of Deuterium Diffusion and Thermal Desorption in Tungsten Exposed to High-Flux Deuterium Plasma

Recent Studies of Tungsten-Based Plasma-Facing Materials in the Linear Plasma Device STEP

He-ion induced surface morphology change and nanofuzz growth on hot tungsten surfaces

Influence of Surface Melting on the Deuterium Retention in Pure and Lanthanum Oxide Doped Tungsten

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Amorphous and Anisotropic Surface Relief Formation in Tungsten under Repeated High-Flux Hydrogen Plasma Loads

Deuterium Retention and Surface Blistering in Non-Damaged and Damaged Tungsten after Repetitive Plasma Exposure and Outgassing

Dislocation Loop and Tangle Evolution of Peak Damage Region in Tungsten Irradiated by Heavy Ion and Deuterium Plasma

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Fluence Dependence of Surface Morphology and Deuterium Retention in W Bulks and Nanocrystalline W Films Exposed to Deuterium Plasma

Observations of Orientation Dependence of Surface Morphology in Tungsten Implanted by Low Energy and High Flux D Plasma

Blistering on Tungsten Surface Exposed to High Flux Deuterium Plasma

Microstructure and Deuterium Retention of Tungsten Deposited by Hollow Cathode Discharge in Deuterium Plasma

Microstructural modification of highly porous resolidified tungsten in heat flux of 46.3 GW/m 2 and focused ion beam