Abstract:In the current study, bulk tungsten material surfaces are exposed to hydrogen, deuterium, and helium plasmas in the radiofrequency domain (13.56 MHz) at an input power of 250 W using the hollow-cathode configuration. The ejected material is collected on titanium substrates at various distances (from 6 mm up to 40 mm). Therefore, the exposed tungsten materials are investigated for surface changes (blister occurrence, dust formation, or nano-structuration), along with the crystallinity, depending on the plasma's exposure times (from 30 min up to 120 min for each plasma type). Also, the collected materials are analyzed (morphological, structural, and statistical investigations) for dust and dust film-like appearance. Plasma discharges are analyzed using two methods: optical emission spectroscopy, and single Langmuir probes, to emphasize the nature of the used plasmas (cold discharges, ~2 eV), along with the presence of tungsten emission (e.g., WI 406.31 nm, WI 421.31 nm) during the plasma lifetime. By using a dedicated protocol, a method was established for obtaining fusion-relevant tungsten surfaces in the hydrogen and deuterium plasma discharges. By using the implemented method, the current paper introduces the possibility of obtaining a new tungsten morphology, i.e., the dandelion-like shape, by using helium plasma, in which the W18O49 compound can be found.

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Enhanced Modification of Tungsten Surface by Nanostructure Formation During High Flux Deuterium Plasma Exposure

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Recent Studies of Tungsten-Based Plasma-Facing Materials in the Linear Plasma Device STEP

Blistering on Tungsten Surface Exposed to High Flux Deuterium Plasma

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Hydrogen Behaviors at the Near-Surface Region of Tungsten: A First-Principles Study

Surface nano structures on W surface exposed to low-energy high flux D plasma

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3 Exposed to Deuterium Plasma

Observations of Orientation Dependence of Surface Morphology in Tungsten Implanted by Low Energy and High Flux D Plasma

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

Subsurface Deuterium Bubble Formation in W Due to Low-Energy High Flux Deuterium Plasma Exposure

Surface Morphology of W Surface Exposed to Low Energy He Plasma at Low Temperature

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Nanostructured fuzz growth on tungsten under low-energy and high-flux He irradiation

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Tungsten Material Behavior under H2, D2, and He Plasma Interaction Conditions in the Framework of Fusion-Relevant Studies

Formation process of tungsten nanostructure by the exposure to helium plasma under fusion relevant plasma conditions