Abstract:Surface modification and deuterium (D) retention in pure tungsten (W) and tungsten-rhenium (W-Re) alloys with Re concentration of 1, 3, 5 and 10 wt.% were investigated after exposure to D plasma with an incident energy of 38 eV/D at about 400 K and various fluences ranging from 7.2 × 1023 to 2.6 × 1025 D/m2. It is found that blistering depends strongly on the exposure fluence for both W and W-Re alloy samples. When the D fluence is higher than 2.8 × 1024 D/m2, the surface of W is covered by two types of blisters. One type is small blisters (<2 μm), which appeared in groups only on grains with surface orientation close to (111). The other type is large-sized (>8 μm) and extents over several grains. In the cases of W-Re alloys, only small blisters can be observed on their surface. The blisters on the surface of W-Re alloys preferentially appeared on grains with surface orientation close to (111). Cross-section views of blisters show that the blisters on W-Re alloys always originate from intra-granular cavities. The small and large blisters on W originate from intra- and inter-granular cavities, respectively. The surface blistering fluence threshold for W-Re alloys is lower than for W. For both types of materials, rupture of blisters occurs if the underlying crack reaches the surface at the edge of a blister. The number of ruptured blisters increases with increasing D fluence. TDS results show that there is an additional high-temperature peak at ∼ 800 K in W-Re alloys. The amount of D released from W and W-Re alloys increases with increasing D fluence. In addition, the accumulation of D in W-Re alloys is not noticeably influenced by the amount of Re doping at the exposure temperature of ∼ 400 K.

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Blistering on Tungsten Surface Exposed to High Flux Deuterium Plasma

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Blister-dominated retention mechanism in tungsten exposed to high-fluence deuterium plasma

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

Dependence of deuterium retention and surface blistering on deuterium plasma exposure temperature and fluence in lanthanum oxide doped tungsten

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Surface Blistering and Deuterium Retention in Chemical Vapor Deposition Tungsten Exposed to Deuterium Plasma

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Surface modification and deuterium retention of tungsten and tungsten-rhenium alloys exposed to deuterium plasma

Enhanced Modification of Tungsten Surface by Nanostructure Formation During High Flux Deuterium Plasma Exposure

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3 Exposed to Deuterium Plasma

Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma

Effect of thickness on the blistering of tungsten exposed to deuterium plasma

Transient grating spectroscopy of thermal diffusivity degradation in deuterium implanted tungsten

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten