Effects of Carbon Deposition on Deuterium Plasma-Driven Permeation Through Tungsten-Coated RAFM Steel
Yue Xu Xiaoping Tian Hongyan Tan Haiying Fu Zheng Gong Junjie Ni Laima Luo a Hefei University of Technology,School of Materials Science and Engineering,Hefei 230009,Chinab Copper Alloy and Forming Engineering Research Center of Ministry of Education,Hefei 230009,Chinac Southwestern Institute of Physics,Center for Fusion Science,Chengdu 610225,Chinad ITER Organization,Route de Vinon-sur-Verdon,CS 90 046,13067 St. Paul Lez Durance Cedex,Francee Liaocheng University,School of Materials Science and Engineering,Liaocheng 252000,China
DOI: https://doi.org/10.1080/15361055.2024.2397220
2024-09-21
Fusion Science & Technology
Abstract:In steady-state operation of fusion reactors, eroded materials and contaminations, especially carbon (C), may deposit on the surface of plasma-facing components. In this work, the effects of C deposition on hydrogen isotope permeation behavior through tungsten (W)–coated reduced activation ferritic/martensitic (RAFM) steel were systematically investigated by plasma-driven permeation (PDP) measurements in the temperature range of 633 to 893 K. A C deposition layer with thickness of ~200 nm was prepared by magnetron sputtering to simulate the formation of C impurities in the first-wall area of tokamaks. The implantation depth of incident deuterium (D) ions was estimated to be <10 nm at incident energy of 114 eV. Deuterium effective diffusion coefficients (D eff 's) for W-coated RAFM steel with/without a C layer were obtained. It was found that the C layer tended to increase D eff in the low-temperature region of ~675 to 820 K. At high temperature, however, D eff was measured be lower than that without a C layer. Nevertheless, the addition of a C layer had no significant effect on D eff compared to the W coating alone with respect to bare RAFM steels. For steady-state D-PDP flux, it was found that the C layer significantly decreased D permeation flux at low temperature. But, the permeation flux difference between the samples with/without a C layer became smaller with increasing temperature, indicating that the influence of C deposition on D permeation was negligible at high temperature. Similar D-PDP behavior was detected as increasing the incident ion flux by means of increasing plasma discharge power. Surface reemission of absorbed D as well as the D concentration gradient throughout the sample was found to be influenced by C deposition; therefore, D permeation flux changed correspondingly.
nuclear science & technology