Abstract:Chemical vapor deposition (CVD) is a promising technique for the preparation of W-based plasma-facing materials (PFMs). An overview of the microstructure, chemical composition, thermal conductivity, thermal stability, thermal shock performance under disruption-like and edge localized mode-like transient heat load, and neutron irradiation performance of CVD-W has been given in our previous work. However, for fusion applications, additional properties need to be assessed. To this end, deuterium (D) permeability, D plasma irradiation performance, and thermal fatigue resistance of CVD-W were investigated in this work. The results showed that the D permeability of CVD-W in the temperature range of 973–1173 K was larger than that of the commercial pure W, which was related to the columnar grain structure of CVD-W. Additionally, both CVD-W and commercial pure W were exposed to D plasma up to a fluence of 1 × 1026 m−2. Compared to commercial pure W, CVD-W exhibited a mitigated blistering behavior and lower D total retention, which could be attributed to its strong [001] crystallographic texture along the thickness direction and a lower number of defect density (e.g. grain boundaries). CVD-W and commercial pure W were also exposed to steady-state and transient heat load simultaneously, leading to a base surface temperature and surface temperature increase of about 953–1473 K and 250–300 K, respectively. A strong grain orientation dependence of the surface degradation induced by the combined heat load has been found. Consequently, CVD-W exhibited a much more uniform plastic deformation than pure W, and no surface cracks along grain boundaries were observed in CVD-W. Finally, the industrial-scale production of CVD-W-based PFMs and mockups was demonstrated. This work paves the way for the fusion applications of thick CVD-W coatings.

Development of New Multi-elements Doped Carbon-base Plasma Facing Materials

A New Type of Multielements-Doped, Carbon-based Materials Characterized by High-thermoconductiv ity, Low Chemical Sputtering, Low RES Yield and Exposure to Plasma

High Heat Flux Testing of B4C/Cu and SiC/Cu Functionally Graded Materials Simulated by Laser and Electron Beam

Surface Diversifying and Deuterium Retention Characteristics of Doped Graphite with SiC Coating Exposed to Plasma Discharges in EAST Tokamak

Processing and Evaluation of Graded SiC/Cu Facing Plasma Composite

New Progress of Ceramic-Based Functionally Graded Plasma-Facing Materials in China

Processing and characterization of B4C/Cu graded composite as plasma facing component for fusion reactors

New Progress of Metal-Based Functionally Graded Plasma-Facing Materials in China

Characteristic and Application Study of Multi-Cathodes Metal Plasma Source

Development of Tungsten As Plasma-Facing Materials by Doping Tantalum Carbide Nanoparticles

Microstructure and Thermal Properties of Inert Plasma-Sprayed Tungsten Coating on SiC-Coated Carbon/Carbon Composites

Fabrication and evaluation of SiC/Cu functionally graded material used for plasma facing components in a fusion reactor

IRRADIATION EXPERIMENTS OF PLASMA FACING MATERIALS DEVELOPED FOR HT-7U IN THE HT-7 TOKAMAK

Advance in Using Plasma Technology for Modification or Fabrication of Carbon‐Based Materials and Their Applications in Environmental, Material, and Energy Fields

Recent progress of thick tungsten coating prepared by chemical vapor deposition as the plasma-facing material

A self-boosting microwave plasma strategy tuned by air pressure for the highly efficient and controllable surface modification of carbon

Dynamic oxidation mechanism of carbon fiber reinforced SiC matrix composite in high-enthalpy and high-speed plasmas

Plasma-target surface interaction during non-equilibrium plasma irradiation at atmospheric pressure: Generation of dusty plasma

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Preliminary R&D on Flat-Type W/Cu Plasma-Facing Materials and Components for Experimental Advanced Superconducting Tokamak