Abstract:Objective Since the development of Yb-doped fiber laser, increasing the output of a single fiber has been one of the most important directions. The output of a single fiber has now been able to attain 10 kW-level or above. However, these results are mainly laboratory reports, and few fibers have been adopted in practical applications because the coating material of these double cladding fibers age quickly due to the injected high pump power and large amount of quantum defect heating. To minimize the impact of high pump power on coating materials, triple-clad Yb-doped fibers, with an addition of fluorine -doped fused silica between silica and low -index coating, have been suggested. For a given fiber, high brightness of the tandem-pumping can not only reduce the quantum defect heating, but also further increase the pump injection and output-power scaling. To achieve a more reliable and higher laser output, a highly Yb-doped triple-clad fiber used for tandem-pumping is proposed. ions The Yb-doped fiber preform has been prepared by modified chemical vapor deposition ( MCVD) in combination with sol-gel solution-doping method to improve the Yb-doped concentration without clusters. The doped preform was overcladded and shaped via grinding in an octagonal shape to form the pump cladding. The preform was further surrounded by the second highly fluorine -doped synthetic fused silica cladding with a depressed refractive index to form the out cladding. Then, the preform was drawn and coated as conventional double cladding fiber to obtain the triple -clad fiber ( Fig. 1). The fiber was characterized by refractive index profiling, electron probe microanalysis (EPMA), loss, and absorption. Finally, the fiber laser performance was characterized. Results and Discussions The fiber is 50/350/400 tan core-clad diameter, 0.06/0.22/0.46 NA, and approximately O. 6 dB/m inner cladding absorption at 1018 nm. The EPMA results showed that the homemade triple -clad fiber has a much higher Yb-doped concentration than the commonly used 20/400 ttm double cladding fiber (Fig. 2). The reduced core numerical aperture was achieved by higher fluorine -doped silica, and laser performance of the fiber was demonstrated by an all -fiber master oscillator power amplifier at 1080 nm. Figure 3 shows the experimental setup; the seed laser is about 600 W, generated via a 20/400 ttm Yb fiber laser oscillator. The triple-clad fiber was used as a gain medium in the power amplifying stage, and the pump sources are 1018 nm fiber lasers. When about 11606 W pump power was absorbed, up to 9010 W laser output with a slope efficiency of 80. 5% was achieved (Fig. 4). Further power scaling was limited by the unabsorbed helical light in the fluorine-doped fused silica cladding, which is round-shaped. Thus, in the high-power laser experiment, only the forward pump was on. In future studies, we will improve the design of fiber laser setup and reduce the pump power in the fluorine-doped silica to further increase the fiber laser output. Conclusions A maximum 9010 W laser output was achieved by the 1018 nm tandem-pumping using the homemade 50/350/400 tan large-mode-area Yb-doped triple-clad fiber. This is an important progress in the field of high-power fiber laser materials. Compared with double cladding fiber, the triple -clad fiber design, which deliveries most of the pump light inside the fluorine -doped fused silica, can greatly minimize the aging effect of the pump light on the coating material. This is of great significance for the long-term operation reliability of high-power laser fiber.

50 Μm Core Diameter Yb^3+/Al^3+/F^− Codoped Silica Fiber with M^2<11 Beam Quality

Silica Nanofibers and Subwavelength-Diameter Fibers

Supercontinuum Generation in Submicrometer Diameter Silica Fibers

Spectroscopic and Laser Properties of Al-P Co-Doped Yb Silica Fiber Core-Glass Rod and Large Mode Area Fiber Prepared by Sol-Gel Method

Mid-infrared dual-cladding photonic crystal fiber with high birefringence and high nonlinearity

66 fs, 3 W all fiber Yb3+-doped mode-locked fiber laser

Double-clad large-mode-area polarization-maintaining ytterbium doped photonic crystal fiber

High ytterbium concentration Yb/Al/P/Ce co-doped silica fiber for 1-μm ultra-short cavity fiber laser application

Large-Mode-Area Neodymium-Doped All-Solid Double-Cladding Silicate Photonic Bandgap Fiber With A 32 Mu M Core Diameter

Single-mode large-mode-area laser fiber with ultralow numerical aperture and high beam quality

~1 Μm Laser Output Based on Heterogeneous Fiber with Yb3+-doped Fluorophosphate Core and Phosphate Cladding

Tm/Al Co-Doped Silica Glass Prepared by Laser Additive Manufacturing Technology for 2-Μm Photonic Crystal Fiber Laser

Growth and Characterization of Yb:Ho:YAG Single Crystal Fiber

Yb 3+ -Doped 200 Μm Diameter Core, Gain Guided Index-Antiguided Fiber

Yb-Doped Triple -Clad Fiber for Nearly 10 Kw Level Tandem-Pumped Output

Yb-Doped Aluminophosphosilicate Laser Fiber

Near diffraction limit output of a coiled 20/400 m Yb-doped fiber laser

All-Solid Silicate Photonic Crystal Fiber Laser with 13.1 W Output Power and 64.5% Slope Efficiency

Yb/Ce Codoped Aluminosilicate Fiber With High Laser Stability for Multi-kW Level Laser

Mid-Infrared 2.79 μm Band Er, Cr: Y3Sc2Ga3O12 Laser Transmission Anti-Bending Low-Loss Anti-Resonant Hollow-Core Fiber

Paving way for fabrication of silica-based single -frequency seed laser: Ultrahighly Yb-doped optical fibers via sol-gel method combined with silica tube inner wall coating and fusion-tapering technique

50 Μm Core Diameter Yb^3+/Al^3+/F^− Codoped Silica Fiber with M^2&lt;11 Beam Quality