Abstract:ZrO2 nanocrystals were synthesised by a microwave-assisted hydrothermal method using zirconium oxychloride (ZrOCl2·8H2O), yttrium chloride (YCl3·6H2O), and liquor ammonia (NH3·H2O) as raw materials, triethanolamine (TEOA) as mineraliser, and polyethylene glycol (PEG) as dispersant. The obtained products were characterised with thermogravimetry-differential scanning calorimetry (TG-DSC), Fourier transform-infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that the concentration of ZrOCl2·8H2O had little effect on the material properties, whereas the PEG molecular weight, microwave hydrothermal time and temperature, and the concentration of TEOA greatly influenced the dispersibility of the nano-sized zirconia powders. XRD and FT-IR analyses indicated that the ZrO2 nanocrystals synthesised by the microwave hydrothermal method had a tetragonal phase without any trace of monoclinic or cubic phases. The optimal parameters for preparing nano-zirconia powders with appreciable crystallinity and crystal forms included the use of PEG1000/PEG2000/PEG4000 dispersants, a microwave hydrothermal time of 30–50 min and a temperature of 200–240 °C, and a TEOA concentration of 0.3–0.5 M. Nano-ZrO2 powder prepared via our optimised microwave hydrothermal method contained mostly tetrahedral, spherically shaped, highly homogeneous, and well-dispersed 20–30 nm particles.

Synthesis and Characterization of Nano-sized Zirconia Powders Using Microemulsion-assisted Wet Solid State Reaction Route

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Preparation of Zirconia Powders by Sol-gel Process

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Nanocrystalline zirconia powder processing through innovative wet-chemical methods

Synthesis and Characterization of Zirconia Nanorods

Phase Composition Controllable Preparation of Zirconia Nanocrystals Via Solvothermal Method

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

A Novel Route for the Preparation of Ultrafine Yttria-Doped Zirconia Powders

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Preparation of ultrafine zirconia powder by emulsion method

Preparation of Zirconia Base Solid Solution Nanopowder by Exothermal Solid-State Synthesis

Preparation and Microstructure of Nanometer Tetragonal Polycrystal Zirconia Powder at Low Temperature Condition

Preparation of nano-sized 6MgO–2Y2O3–ZrO2 powders by a combined co-precipitation and high energy ball milling process

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

Preparation of Nano-Sized Biomedical ZrO2 Particles with Microemulsion Method

Preparation and Characterization of Nano-Sized Al2O3/ZrO2 Powders

Supercritical Hydrothermal Synthesis of Nano-Zirconia: Reaction Path and Crystallization Mechanisms of Different Precursors

Mechanochemical dehydration and crystallization of supersaturated zirconia–alumina composite nano powders