Abstract:The corrosion and leakage issues of rapid quench boilers have become increasingly prominent in ethylene plants, significantly disrupting the regular functioning of equipment. In pursuit of a more efficacious corrosion protection strategy, a study was conducted on the heat exchange tubes experiencing corrosion leakage in the quenching boiler of a petrochemical company. By means of macroscopic observation, chemical composition analysis, mechanical property analysis, metallographic analysis, fracture surface morphology observation, and energy spectrum analysis, combined with on-site process parameters, a comprehensive analysis of the failure causes of the corroded leakage sites was conducted. It was concluded that the perforation of the heat exchange tubes was caused by high-temperature oxygen corrosion and oxidation induced by scale accumulation, and reasonable countermeasures were proposed. According to X-ray diffraction analysis (XRD), it was found that the scale mainly consisted of Fe2O3 and Fe3O4, and the scale formation time was relatively long. It is speculated that the accumulation of scale is caused by the rust from the upstream equipment pipelines of the boiler water being carried into the quenching boiler with the fluid flow and accumulating at this location. Regarding the heat exchange tubes, the primary causes of failure are high-temperature oxygen corrosion and oxidation. To verify whether the relevant reactions can occur spontaneously, the critical transition temperature of the reactions is calculated using the free entropy function method. The calculated critical temperature for the occurrence of high-temperature oxygen corrosion and oxidation in the heat exchange tubes under failure conditions is determined to be T ＜ 1058 K ~ 785 °C. Therefore, under the conditions of heat exchange tube failure, high-temperature oxygen corrosion and oxidation can occur spontaneously.

Cause and Remedy for Cracks in Weld Seams of Reheater Sealing Plate of Wall Type for 350 MW Power Generating Set Boiler

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

Analysis on the cause of crack in connection pipeline of subcritical boiler reheater

Study on Stress Intensity of Welding Parts of Small Dlameter Tube to Reheater in Coal-burning Thermo-electric Factory with 200 MW Power

Cause analysis of elbow crack for header's connecting tubes of boiler's reheater concerning 300 mw unit

Cause and mechanism analysis of cracking and leakage of water wall tube

Study of the Reason and Measure on One 300MW Reheat Pipe Weld Bead's Blasting & Leaking

Root cause analysis of a cracked primary heat exchanger in a gas wall-mounted boiler

Cause Analysis and Improvement Measures for Pipeline Cracking of 9Cr-1Mo Material

Failure analysis of a rapid quench boiler for ethylene cracker

Analysis on reason of tube cracking of platen superheater during commissioning of supercritical boiler

Analysis and Repair of Cracks in Welding Tee of Main Steam Pipelines in Thermal Power Units

Water Wall Tubes’ High Temperature Corrosion Root Cause Investigation: A 300 MW Level Boiler Case

Failure analysis of reheater tubes in a 350 MW supercritical circulating fluidized bed boiler

Cracking Analysis on Water Cooling Wall Pipe in Power Plant

Causes Leading to Bulge Failure of Aluminized Water Wall Tube and Countermeasure for Quick Treatment

Reason Analysis and Countermeasures for Leakage of Middle-pressure Waste Heat Boiler

Analysis of the Vibration Damage Mechanism of the Tube Bundles of a Glycol Re-Boiler

Leakage of water-cooled wall tube in subcritical boiler

Failture Analysis of Welded Joint on Superheater of a 670t/h Boiler

Corrosive damage analysis and characterization of boiler tubes in a secondary superheater