Abstract:The corrosion and leakage issues of rapid quench boilers have become increasingly prominent in ethylene plants, significantly disrupting the regular functioning of equipment. In pursuit of a more efficacious corrosion protection strategy, a study was conducted on the heat exchange tubes experiencing corrosion leakage in the quenching boiler of a petrochemical company. By means of macroscopic observation, chemical composition analysis, mechanical property analysis, metallographic analysis, fracture surface morphology observation, and energy spectrum analysis, combined with on-site process parameters, a comprehensive analysis of the failure causes of the corroded leakage sites was conducted. It was concluded that the perforation of the heat exchange tubes was caused by high-temperature oxygen corrosion and oxidation induced by scale accumulation, and reasonable countermeasures were proposed. According to X-ray diffraction analysis (XRD), it was found that the scale mainly consisted of Fe2O3 and Fe3O4, and the scale formation time was relatively long. It is speculated that the accumulation of scale is caused by the rust from the upstream equipment pipelines of the boiler water being carried into the quenching boiler with the fluid flow and accumulating at this location. Regarding the heat exchange tubes, the primary causes of failure are high-temperature oxygen corrosion and oxidation. To verify whether the relevant reactions can occur spontaneously, the critical transition temperature of the reactions is calculated using the free entropy function method. The calculated critical temperature for the occurrence of high-temperature oxygen corrosion and oxidation in the heat exchange tubes under failure conditions is determined to be T ＜ 1058 K ~ 785 °C. Therefore, under the conditions of heat exchange tube failure, high-temperature oxygen corrosion and oxidation can occur spontaneously.

Reason Analysis and Countermeasures for Leakage of Middle-pressure Waste Heat Boiler

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

Cause and mechanism analysis of cracking and leakage of water wall tube

Failure Analysis on Abnormal Corrosion of Economizer Tubes in a Waste Heat Boiler

Study on Stress Intensity of Welding Parts of Small Dlameter Tube to Reheater in Coal-burning Thermo-electric Factory with 200 MW Power

Failure Analysis on Abnormal Leakage of Shell and Tube Heat Exchanger in Specialty Chemical Plant

Study of the Reason and Measure on One 300MW Reheat Pipe Weld Bead's Blasting & Leaking

Analysis of the Vibration Damage Mechanism of the Tube Bundles of a Glycol Re-Boiler

Analysis of Causes and Protective Measures against Corrosion Perforation in the Shell-Side Outlet Flange of a Sour Water Steam Heater

Failure analysis of a rapid quench boiler for ethylene cracker

Corrosion failure analysis of the heat exchanger in a hot water heating boiler

Failure Analysis on Abnormal Leakage Between Tubes and Tubesheet of Spiral-Wound Heat Exchanger for Nuclear Power Plant

Leakage of water-cooled wall tube in subcritical boiler

Failure Analysis and Countermeasure of Heat Exchangers in Nuclear Power Facility

Failure Analysis on Leaked Jacket Pipe of Double-Pipe Heat Exchanger in High-Pressure Polyethylene Facility

Failture Analysis of Welded Joint on Superheater of a 670t/h Boiler

Corrosive damage analysis and characterization of boiler tubes in a secondary superheater

FAILURE ANALYSIS OF BOILER TUBE

Analysis of Invalidation Mechanism of Reheater of 1100t/h Boiler

FaiIure Behavior AnaIysis of Hydrocracker Heat Exchanger and Its Countermeasures

Failure Analysis on Abnormal Bursting of Heat Transfer Tubes in Spiral-Wound Heat Exchanger for Nuclear Power Plant