Abstract:Iron-based superconductors, characterized by a high upper critical field and small anisotropy, have been regarded as prospective candidate material for high magnetic field applications. For such applications, it is essential to develop iron-based superconducting wires and tapes with high in-field critical current density (Jc). In view of material microstructure, large-sized superconducting grains with high-degree of grain texture are preferable for high efficiency current transportation, but on the other hand will sacrifice some grain boundaries that act as potential flux pinning centers. Here, based on powder-in-tube method, a novel approach combining medium temperature pressing and hot isostatic pressing was developed for the fabrication of Cu/Ag composite sheathed (Ba, K)Fe2As2 (Ba-122) iron-based superconducting tapes. Microstructural analysis reveals lager grain size and improved grain texture produced by the combined processes, and at the same time, high-density nano-size dislocations were induced in grains, which further enhanced the current carrying ability at high field region. As a result, high transport Jc of 1.6×105A /cm2 at 4.2K and 10T was obtained for the Ba-122 tapes, and more importantly, due to the significantly reduced field dependence of Jc, the transport Jc was still kept above the practical level of 105A /cm2 at high fields up to 25T. At 25T, the value of Jc exceeds 60% of its value at 10T, indicating a minimal reduction in iron-based superconducting wires and tapes. This study demonstrates a favorable microstructure that will help to approach superior current transport performance under high magnetic fields for iron-based superconductors.

Development of Metal-Insulated Iron-Based Superconducting Coils and Charging Tests under High Magnetic Fields Up to 32 T

Development of the Iron-Based Superconducting Coils for High Magnetic Field Application

Performance testing of the iron-based superconductor inserted coils under high magnetic field

Fabrication and Test of Diameter 35 Mm Iron-Based Superconductor Coils

First Performance Test of a 30 Mm Iron-Based Superconductor Single Pancake Coil under a 24 T Background Field

Development of the first Tesla class iron-based superconducting coil for high field application

Investigation of the Energizing Characteristics of a Metal-Insulation Iron-Based Superconducting Coil

First Performance Test Of The Iron-Based Superconducting Racetrack Coils At 10 T

High Transport Current Superconductivity in Powder-in-tube Ba0.6K0.4Fe2As2 Tapes at 27T

Recent Breakthrough Development in Iron-Based Superconducting Wires for Practical Applications

Iron-based superconducting materials for high-field applications

Effect of Bending Before Annealing on Current-Carrying Properties of Iron-Based Superconducting Tapes

Investigation of Normal Zone Propagation Velocity in AgSn/Ag/Ba122 Superconducting Tapes Using a Conduction Cooling Test System

Development of high-performance iron-based superconducting wires and tapes

Development of Multi Field Test System for High Temperature Superconducting Tapes

First Performance Test of FeSe0.5Te0.5 Coated Conductor Coil under High Magnetic Fields

Performance Investigation of a New Developed High-Jc Nb3Sn Superconducting Strand

Recent development of the 25 T all-superconducting magnet at IEE

Superior Transport Current Densities in (ba, K)Fe2As2 Superconducting Tapes Realized by Combined Strengthening of Grain Texture and Flux Pinning

High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process

High Critical Current Density in Cu/Ag Composited Sheathed Ba0.6K0.4Fe2As2 Tapes Prepared Via Hot Isostatic Pressing