Abstract:The future fusion reactor devices built by Institute of Plasma Physics, Chinese Academy of Science (ASIPP) will be a compact burning plasma facility to fill the gap between ITER and the China Fusion Engineering Test Reactor (CFETR), with the mission of studying the Deuterium-Tritium (D-T) plasma in steady-state operation. The winding-package (WP) of its toroidal field coil (TFC) is graded into high-field WP and low-field WP, and the high critical current density (J c ) Nb 3 Sn strand will be applied to the high-field WP based on the current design. The thermo-magnetic instability is the main issue in the application of high-J c Nb 3 Sn strand, which may induce premature quenching in the low field regions. This issue can be improved by reducing the effective filament diameter to suppress flux jumps and increasing the residual resistivity ratio (RRR) to enhance the release of heat generated by flux jumps. However, in the conductor manufacturing process, local plastic deformations of strands can impact the sub-element layout and degrade the RRR of the strand, which would increase again the risk on instability. In this study, magnetization measurements and V-I tests were performed on samples with different indentation depths. The hysteresis loss and d eff of the indented sample was obtained from the test results. The impact of local plastic deformation on the thermo-magnetic instability of two types of Nb 3 Sn strand was confirmed by cross-sectional metallographic observation and quantitative microstructure analysis. It was shown that flux jumps were suppressed at indentation depths below 0.3 mm. Further indentation increase leads to severe flux jumps.

Performance Investigation of a New Developed High-Jc Nb3Sn Superconducting Strand

An Investigation Into The Heat Treatment Tolerance Of Wst Nb3sn Strands Produced For Massive Fusion Coils

Characterization Of Nb3sn Strands For A 40-T Hybrid Magnetic Model Coil

Characteristics of New Nb 3 Sn Strand Developed in Korea for High Field Applications

Internally Oxidized Nb3Sn Strands with Fine Grain Size and High Critical Current Density

Development Of Nb3sn Superconducting Coil Manufacture Technology

Impact of local plastic deformation on thermo-magnetic instability of high-J c Nb 3 Sn strand

Development of Electromagnetic Forming Nbti Superconducting Joint

Characterization of $\hbox{Nb}_{3}\hbox{Sn}$ Strands for a 40-T Hybrid Magnetic Model Coil

Impact of Transverse Compression on the Sub-Element RRP Nb3Sn Strand

Impact of Local Plastic Deformation on Thermo-Magnetic Instability of High-J C Nb3Sn Strand

Fabrication and Test of Nb3Sn-NbTi Superconducting Joint for a 14-T MRI Magnet

Effect of Nb3Sn Coarse Grains on Critical Current Densities of Internal Tin Nb3Sn Strand

Development of Metal-Insulated Iron-Based Superconducting Coils and Charging Tests under High Magnetic Fields Up to 32 T

Experimental Study on A Nb3al Insert Coil under High Magnetic Field

DC Performance Measurement and Assessment of Nb 3 Sn Cable-In-Conduit Conductor for CFETR CS Model Coil

The cryogenic experiment for the Nb3Sn CICC model coil and the analysis of its strain test results

Research Progress of Nb3Al Superconducting Wire for High-Field Application

Mechanical Design of a Nb3Sn Superconducting Magnet System for a 45 GHz ECR Ion Source

Experiment of Joints Resistance and Critical Current of Bi2212 Conductor

Research on Insulation Technology for Nb3Sn Layer Coil of Superconducting Conductor Testing Facility