Abstract:Ba x K1−x Fe2As2 (BaK-122) iron-based superconductors (IBSs) have been considered to be promising for high-field applications. The transport J c performance of BaK-122 wires and tapes is continuously enhanced by introducing advanced fabricating methods. The mass density of BaK-122 superconducting core in wires and tapes is important to the transport J c performance and related to the mechanical behavior during preparation. In this work, the mechanical property parameters including Poisson’s ratio-density, yield strength-density, and elastic modulus-density of BaK-122 IBS powder were examined via uniaxial compression experiments. The density-dependent mechanical constitutive of BaK-122 was obtained for the first time. The relationship function between density and Vickers hardness of BaK-122 was established as HV0.05 = 0.0249ρ 5.332 based on the numerical simulation of hardness testing, and a method for characterizing the BaK-122 core density was developed. It had been found the sheath materials and preparation method have great influences on the stress state of the BaK-122 core, and then affect the density. The densification mechanism and corresponding improvement method were revealed to provide guidance for preparing high-density BaK-122 wires and tapes. Finally, the generalized relationship between density and the superconducting transport J c was established according to lots of experimental data from multiple BaK-122 samples, which has confirmed the positive correlation of ρ core and J c. We comparatively discussed the various cold-work and heat-treatment processes used in our team for preparing the BaK-122 wires and tapes, and the critical factors affecting the transport performance were summarized.

First Performance Test of a 30 Mm Iron-Based Superconductor Single Pancake Coil under a 24 T Background Field

Fabrication and Test of Diameter 35 Mm Iron-Based Superconductor Coils

Performance testing of the iron-based superconductor inserted coils under high magnetic field

Development of Metal-Insulated Iron-Based Superconducting Coils and Charging Tests under High Magnetic Fields Up to 32 T

First Performance Test Of The Iron-Based Superconducting Racetrack Coils At 10 T

Development of the first Tesla class iron-based superconducting coil for high field application

Development of the Iron-Based Superconducting Coils for High Magnetic Field Application

High Transport Current Superconductivity in Powder-in-tube Ba0.6K0.4Fe2As2 Tapes at 27T

First Performance Test of FeSe0.5Te0.5 Coated Conductor Coil under High Magnetic Fields

Iron-based superconducting materials for high-field applications

Investigation of the Energizing Characteristics of a Metal-Insulation Iron-Based Superconducting Coil

Superconducting Properties of 100-M Class Sr0.6K0.4Fe2As2 Tape and Pancake Coils

High Transport Jc in 7-Filament Cu/Ag Sheathed Ba0.6K0.4Fe2As2 Tapes Manufactured by Ambient Pressure Sintering

Development of a Bi-2212 Solenoid Insert Coil in a 12 T Superconducting Magnet

Mechanical Properties and Densification Mechanism of Powder-in-tube Ba X K1−x Fe2As2 Superconductors

Progress in the Development of the 122-Type IBS Wires

Development of high-performance iron-based superconducting wires and tapes

High Critical Current Density in Cu/Ag Composited Sheathed Ba0.6K0.4Fe2As2 Tapes Prepared Via Hot Isostatic Pressing

Performance Investigation of a New Developed High-Jc Nb3Sn Superconducting Strand

Iron-Based Superconductors for High-Field Applications: Realization of High Engineering Critical Current Density

Recent Breakthrough Development in Iron-Based Superconducting Wires for Practical Applications