Abstract:Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly attractive for high-field applications, especially in particle accelerator magnets, nuclear magnetic resonance spectrometers, medical magnetic resonance imaging systems and nuclear fusion reactors. Herein, through an industrially scalable and cost-effective manufacturing strategy, a practical level critical current density up to 1.1x10^5 A/cm2 at 4.2 K in an external magnetic field of 10 T was achieved in Cu/Ag composite sheathed Ba0.6K0.4Fe2As2 superconducting tapes. The preparation strategy combines flat rolling to induce grain texture and a subsequent hot-isostatic-pressing densification. By varying the parameters of rolling, the degree of grain texture was engineered. It is found that the transport properties of the Ba1-xKxFe2As2 tapes can be enhanced by applying a large amount of deformation during rolling, which can be attributed to the improved degree of c-axis texture. Microstructure characterizations on the highest-performance tape demonstrate that the Ba1-xKxFe2As2 phase has a uniform element distribution and small grains with good connectivity. Grain boundary pinning is consequently enhanced as proved by large currents circulating through the sample even at 25 K. Our work proves that Cu/Ag composite sheathed Ba1-xKxFe2As2 superconducting tapes can be a promising competitor for practical high-field applications in terms of the viable, scalable and cost-effective fabrication strategy applied and the high transport properties achieved in this work.

High Transport Current Superconductivity in Powder-in-tube Ba0.6K0.4Fe2As2 Tapes at 27T

Iron-Based Superconductors for High-Field Applications: Realization of High Engineering Critical Current Density

Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes

High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process

Interface effects on current transport properties in multi-layered (Ba, K)Fe2As2 superconducting wires

Development of high-performance iron-based superconducting wires and tapes

Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes

Low field anomaly in the critical current of Ba1‐xKxFe2As2 tapes

High-performance Ba1-xKxFe2As2 superconducting tapes with grain texture engineered via a scalable and cost-effective fabrication

Role of heat and mechanical treatments in the fabrication of superconducting Ba0.6K0.4Fe2As2 ex-situ Powder-In-Tube tapes

Enhancement of critical current densities in (Ba,K)Fe2As2 wires and tapes using HIP technique

Enhancement of Critical Current Densities in (Ba,K)Fe2As2 by 320 MeV Au Irradiation in Single Crystals and by High-Pressure Sintering in PIT Wires

Properties of seven-filament Cu/Ag-sheathed (Ba,K)Fe2As2 tapes fabricated from round and square wires

Fabrication and Transport Properties of 100 m Class Sr0.6K0.4Fe2As2 Wires and Pancake Coils

High tolerance of the superconducting current to large grain boundary angles in potassium-doped BaFe 2 As 2

Enhanced mechanical strength and texture of (Ba,K)Fe 2 As 2 Cu/Ag composite sheathed tapes with Nb barrier layer

Fabrication and characterization of iron pnictide wires and bulk materials through the powder-in-tube method

Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes

High critical current density in low-cost iron-based superconducting round wires annealed at ambient pressure

High, Magnetic Field Independent Critical Currents In (Ba,K)Fe2as2 Crystals

High-performance Ba1-xKxFe2As2 superconducting joints for persistent current operation