Study on Performance and Electrodeposition Process of Ni-P-W-WC Composite Coatings

Yuan Lin

IF: 1.8

2007-01-01

Materials Science and Technology

Abstract:Ni-P-W-WC composite coatings were processed by electrodeposition and their performance were studied.The effect of content of C,deposition rate and surface of coatings on current densities,times of deposition,content of WC and sodium tungstale in electrolysis were studied by the index of content of WC,deposition rate and surface of coating.The operation conditions of composite coating were optimized: a Ni sheet was used as anode,time of electrodeposition was 40 min,the contents of WC in electrolysis were 14 g/L,the content of sodium tungstate in electrolyses were 120 g/L,PH:4.0,current densities were 4.0 A/dm2,and surface microstructure,corrosion resistance and resistance to oxidation of composite coatings were tested by SEM,XRD,and the current-potential curve et.Results show that the performance of Ni-P-W-WC composite coating is better compared with NI-P-W composite coating.