Abstract:This study aims to enhance the surface toughness and overall performance of arc-shaped nail teeth, which are vital components of presowing film-recovery machinery. Laser cladding technology was employed to deposit Ni60A/Cr3C2 composite coatings with the rare-earth oxide Y2O3 onto 60Si2Mn steel surfaces. The effects of different amounts of Y2O3 on the wear resistance of Ni60A/Cr3C2 composite coatings were evaluated. Scanning electron microscopy (SEM), X-ray diffraction, X-ray photoelectron spectroscopy, and 3D morphological analysis were used to investigate the microstructure, microhardness, elemental distribution, and tribological properties of the coatings. The ideal amount of Y2O3 to add to the mixtures to enhance the wear resistance was determined. The results showed that the coating containing 1.5% Y2O3 and Ni60A/Cr3C2 composite powder exhibited superior overall performance. Coatings with different amounts of added Y2O3 exhibited similar phase compositions, mainly consisting of γ-Ni-based, Ni2Si, M7C3 (M = Cr, Mn), and M23C6-strengthened phases. SEM analysis revealed that the coating with 1.5% Y2O3 exhibited excellent metallurgical bonding with the substrate. In addition, the coating exhibited finer grains, increased density, a more uniform distribution of coating elements, and a microhardness of 990 HV. Fewer grooves and smoother abrasions were observed after the wear test. The wear amount and depth were 14 × 10−4 g and 8.97 μm, which were 22.2% and 55.4% lower than the coating without added Y2O3, respectively. The tribological behavior indicated that adding the appropriate amount of Y2O3 facilitated the grain boundary consolidation while enhancing the adhesive properties of the oxide film, thereby increasing the wear resistance of the coating.

Investigation on Microstructure and Tribological Performances of Electrodeposited Ni-W-Y2O3 Composite Coatings

Influence of Y2O3 Nanoparticles on Microstructures and Properties of Electrodeposited Ni–W–Y2O3 Nanocrystalline Coatings

Preparation and Tribological Performance of Electrodeposited Ni-Tib2-Dy2o3 Composite Coatings

Synthesis and Tribological Behavior of Electroless Ni–P–WC Nanocomposite Coatings

Investigation on Microstructure and Properties of Electrodeposited Ni-Ti-CeO2 Composite Coating

Nanostructured Ni–WC–Co composite coatings fabricated by electrophoretic deposition

Effect of Y2O3 content on microstructure and properties of Ni-based self-lubricating composite coating

Microstructure And Properties Of Ni-Co-Tio2 Composite Coatings Fabricated By Electroplating

Tribological Properties and Corrosion Resistance of Porous Structure Ni-Mo/ZrO2 Alloys

Synthesis and Characterization of Ni–Al–Y2O3 Composite Coatings with Different Y2O3 Particle Content

Effect of Y2O3 addition on the organization and tribological properties of Ni60A/Cr3C2 composite coatings obtained by laser-cladding

Preparation and Tribological Behavior of Electrodeposited Ni–W–GO Composite Coatings

Influence of Ti3C2Tx Addition on the Corrosion Behaviour and Tribological Properties of Electrodeposited Ni-W-Ti3C2Tx Nanocomposite Coatings

Investigating the Microstructure and Anti-corrosion Behavior of the Electroless Ni-P-Y2O3 Composite Coatings

Wear and corrosion mechanisms of Ni–WC coatings modified with different Y2O3 by laser cladding on AISI 4145H steel

Preparation, Microstructure and Tribological Properties of Nano-Al2o3/Ni Brush Plated Composite Coatings

Effect of Surface Roughness and Structure Features on Tribological Properties of Electrodeposited Nanocrystalline Ni and Ni/Al2O3 Coatings

Microstructure and Properties of Ni-P Electroless Composite Coating Added with Nano-TiO2

Electrodeposition of Ni-WC composite coatings: formation, structure and properties

Electrodeposition and Tribological Properties of Ni–SrSO4 Composite Coatings

Wear and Friction Properties of Electrodeposited Ni-Based Coatings Subject to Nano-enhanced Lubricant and Composite Coating