Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Preparation and Tribological Behavior of Electrodeposited Ni–W–GO Composite Coatings

Preparation and Properties of Electrodeposited Ni-B-Graphene Oxide Composite Coatings

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Preparation and Properties of Ni–W Composite Coatings Reinforced by Graphene Nanoplatelets

Corrosion resistance and tribological behavior of FeCoCrNi@GO/Ni high entropy alloy-based composite coatings prepared by electrodeposition

Study on the use of furan epoxide modified graphene to enhance the corrosion resistance and wear resistance of electroless Ni-W-P coatings

Dry Sliding Tribological Behaviors of Electrodeposited Ni-GO/SiC Composite Coating on the 2218 Aluminum Alloy

Corrosion Resistance and Micro-Tribological Properties of Nickel Hydroxide-Graphene Oxide Composite Coating

Hydrophobic Reduced Graphene Oxide-Based Ni Coating for Improved Tribological Application

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

The Effect of Plasma Nitriding Time on the Tribological and Mechanical Properties of Electroless Nickel–Boron-Reduced Graphene Oxide (Ni–B-rGO) Nano-Composite Coatings

High-performance anti-corrosion behavior of graphene oxide decorated nickel coating by novel ultrasonic-assisted supercritical-CO2 electrodeposition approach

Hardness and tribological properties of co-electrodeposited Ni-W-B/B coatings

The Development of Novel Cu/GO Nano-Composite Coatings by Brush Plating with High Wear Resistance for Potential Brass Sliding Bearing Application

Anticorrosion behavior and enhanced wear resistance of Ni–P–GO–Y composite coating on the surface of NdFeB permanent magnet

Preparation and tribological properties of Ni-P electroless composite coating containing inorganic fullerene-like WS2 nanomaterials

Fabrication of In Situ rGO Reinforced Ni-Al Intermetallic Composite Coatings by Low Pressure Cold Spraying with Desired High Temperature Wear Characteristics

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings

Electrodeposition of Ni-WC composite coatings: formation, structure and properties

Preparation of laminar α-ZrP nanosheets enhanced Ni W nanocomposite coating and investigation of its mechanical and anti-corrosion properties

Wear resistance of Ni/nano-Al2O3 composite coatings by brush electroplating