Abstract:In this study, Ni/nano-Al 2 O 3 composite coatings and the Ni/Ni–Al 2 O 3 multilayer coatings have been prepared on the 304 stainless steel substrate by adding the nano-Al 2 O 3 particle in Ni plating solution and by alternately brush electroplating, respectively. The microstructure, hardness and wear resistance of the composite and multilayer coatings were studied. Results showed that adding Al 2 O 3 nanoparticle in coatings significantly influences the size and growth direction of grain. The Al 2 O 3 content and hardness of coatings first increased, reached a maximum value of 603 HV and then decreased with the increase in the addition of Al 2 O 3 nanoparticle in Ni plating solution. The friction coefficient, wear loss and wear rate showed an opposite trend. In terms of mass loss and wear rate, the wear resistance of coating increases with increasing Al 2 O 3 content in coatings. An appropriate addition (20–25 g L −1 ) of Al 2 O 3 nanoparticles can effectively enhance the wear resistance of the brush electroplating Ni coating. The minimum wear rate is 2.2–2.3 10 −5 mm 3 N −1 m −1 . The multilayer structure coatings can prevent or delay microcrack initiation and growth by layer interface and grain boundary and increase the thickness of coatings without cracks. The multilayer coatings possessed the approximately same hardness (595 HV) and tribological properties compared with monolayer coatings.

Wear resistance of Ni/nano-Al2O3 composite coatings by brush electroplating

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

Technology for Ni-Al2O3 Composite Coating and Its Properties

Effect of nano-Al 2 O 3 particle addition on Co–P–xAl 2 O 3 nanocomposite plating electroplated on X65 steel

The Wear Resistance of an Ni-Cu-P Brush Plating Layer on Different Substrates

Microstructure of Nanometer-sized Al2O3 Composite Coating Prepared by Electroless Plating

Synthesis of Ni/nano-Al 2 O 3 coatings by brush plating with magnetic fields

Strengthening effect of α-ZrP nanosheet inclusions on corrosion resistance and wear resistance of Ni P deposits

Effect of Surface Roughness and Structure Features on Tribological Properties of Electrodeposited Nanocrystalline Ni and Ni/Al2O3 Coatings

Preparation of Ni-Cnt Composite Coatings on Aluminum Substrate and Its Friction and Wear Behavior

Enhanced Mechanical and Tribological Capabilities of a Silicon Aluminum Alloy with an Electroplated Ni–Co–P/Si3N4 Composite Coating

Study on Ni-P-nanoTiN Electroless Composite Coating

Effects of Ni-5 wt% Al/Bi2O3 addition and heat treatment on mechanical and tribological properties of atmospheric plasma sprayed Al2O3 coating

Microstructure and mechanical properties of electroless Ni–P–Si 3 N 4 –TiN composite coatings

Microstructure and Wear Resistance of a Composite Coating Prepared by Laser Alloying with Ni-Coated Graphite on Ti-6Al-4V Alloy

Tribological performance and high temperature oxidation behaviour of thermal sprayed Ni- and NiCrAlY-based composite coatings

Microstructure, mechanical properties and tribological behaviors of TiAlN-Ag composite coatings by pulsed magnetron sputtering method

Efficiency of Application of (Mo, Al)N-Based Coatings with Inclusion of Ti, Zr or Cr during the Turning of Steel of Nickel-Based Alloy

Development and Characterization of Magnetron Sputtered Self-Lubricating Au-Ni/a-C Nano-Composite Coating on CuCrZr Alloy Substrate

Fabrication and wear property of NiCo coated ZrO2–Al2O3 ceramic particles reinforced high manganese steel-based composites