Abstract:Marine and coastal infrastructures usually suffer from synergetic effect of corrosion and wear known as tribocorrosion, which imposes strict requirements on the structural materials used. To overcome this problem, novel composite wear- and corrosion-resistant xTiC-Fe-CrTiNiAl coatings with different TiC content were successfully developed. The coatings were obtained by the original technology of electrospark deposition in a vacuum using xTiC-Cr2Ti-NiAl (x = 0, 25, 50, 75%) electrodes. The structure and morphology of the coatings were studied in detail by XRD, SEM, and TEM. The effect of TiC content on the tribocorrosion behavior of the coatings was estimated using tribological and electrochemical (under stationary and wear conditions) experiments, as well as impact testing, in artificial seawater. The TiC-free Fe-Cr2Ti-NiAl coating revealed a defective inhomogeneous structure with transverse and longitudinal cracks. Introduction of TiC allowed us to obtain coatings with a dense structure without visible defects and with uniformly distributed carbide grains. The TiC-containing coatings were characterized by a hardness and elastic modulus of up to 10.3 and 158 GPa, respectively. Formation of a composite structure with a heavily alloyed corrosion-resistant matrix based on α-(Fe,Cr) solid solution and uniformly distributed TiC grains led to a significant increase in resistance to stationary corrosion and tribocorrosion in artificial seawater. The best 75TiC-Fe-CrTiNiAl coating demonstrated the lowest corrosion current density values both under stationary (0.03 μA/cm2) and friction conditions (0.8 μA/cm2), and was characterized by both a 2-2.5 times lower wear rate (4 × 10−6 mm3/Nm) compared to AISI 420S steel and 25TiC-Fe-CrTiNiAl and a high fracture toughness.

Microstructure And Properties Of Ni-Co-Tio2 Composite Coatings Fabricated By Electroplating

Mechanical and Corrosion Resistance Properties of Tio2 Nanoparticles Reinforced Ni Coating by Electrodeposition

Microstructure and properties of Cu-Sn-Zn-TiO2 nano-composite coatings on mild steel

Influence of Ti3C2Tx Addition on the Corrosion Behaviour and Tribological Properties of Electrodeposited Ni-W-Ti3C2Tx Nanocomposite Coatings

Enhanced wear resistance of Ni-Mo-TiN composite coating by synergistic effect of tough Ni-Mo matrix and hard TiN particles

Preparation and properties of Ni-W-P-TiO2 nanocomposite coatings developed by a sol-enhanced electroplating method

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Deposition and properties of plasma sprayed NiCrCoMo–TiC composite coatings

Influence of the bath pH value on the microstructure and properties of a novel electrodeposited Ni-W-Ti3C2TX composite coating

Tailoring role of Al and Ti particles in the microstructure and property of electrodeposited Ni matrix nanocomposite coatings

Preparation and Characterization of Nanostructured Ni-TiN Composite Films

Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Study on Ni-P-nanoTiN Electroless Composite Coating

Microstructure and Tribological Properties of WC/Ni-MoS2 Titanium-Based Composite Coating on TC4

An Investigation into Electrodeposited Co−Ni−TiO2 Films with Improved Mechanical and Corrosion Properties

The Influence of Pulse Plating Parameters on the Structure and Corrosion Behavior of Ni-W-TiC Nanocomposite Coatings

Microstructure and tribological properties of electrodeposited Ni–Co alloy deposits

Influence of TiC Addition on Corrosion and Tribocorrosion Resistance of Cr2Ti-NiAl Electrospark Coatings

Microstructure and mechanical properties of electroless Ni–P–Si 3 N 4 –TiN composite coatings

Tribological performance and high temperature oxidation behaviour of thermal sprayed Ni- and NiCrAlY-based composite coatings