Abstract:In this study, a novel technique of consecutive multi-pass cooperative lowered-temperature rolling (CMCLR) was proposed for the first time, with the purpose of preparing high performance wrought magnesium alloys. Based on this, a highly ductile magnesium alloy sheet could be effectively produced from ingot. The corresponding microstructure could directly evolve from coarse dendrites to equiaxed grains with an average size of similar to 5 mu m, which was attributed to the intense dynamic recrystallization (DRX) during isothermal deformation. The equivalent strain gradually decreased from the surface to the interior and edge of the rolled sheet due to the anisotropic plastic deformation. Instead, the temperature of the core of the sheet was slightly higher than that of the surface due to the deformation heat effect. The basal texture in the RD-TD plane generally weakened in the form of the splitting of basal texture toward the RD and the broadening of basal plane away from the pole center due to texture randomization dominated by DRXed grains. The exceptional ductility of more than 28.7% together with acceptable ultimate tensile strength of not less than 267 MPa was ascribed to the progressive work hardening as a result of seamless switching of multiple deformation modes, i.e., basal dislocation-slip-mediated deformation was preferentially operated and then was substituted by twinning-controlled deformation and non-basal dislocation-slip-dominated deformation. The selection of {10 (1) over bar2} twin variants agreed well with geometrical compatibility factor (m') criterion instead of Schmid's law. The activated twin variants nearly engulfed the whole parent grains for the sake of preserving compatible deformation continuity at ambient temperature, giving rise to the formation of TD-split texture. Comparatively, the {10 (1) over bar2} twinning could randomize the basal texture via reorienting grain orientations which in turn facilitated the reactivation of dislocation slip systems in the case of high temperature deformation.

Towards enhancing the ductility of AZ31 Mg alloys by controlling twin orientation at various shear strain levels

Unveiling the ductility enhancement mechanisms in AZ31 magnesium alloy achieved via shear strain-assisted twin orientation regulation

Influence of In-Plane Simple Shear Strain on the Grain Orientation Regulation and Stretch Formability of Pre-twinned AZ31 Magnesium Alloy Sheet

Effect of Induced Screw Twisted Strain on the Twin Orientation Regulation and the Ductility of Pre-Twined ZM21 Mg Alloys

Achieving High Ductility and Low In-Plane Anisotropy in Magnesium Alloy Through a Novel Texture Design Strategy

Enhanced Stretch Formability of AZ31 Magnesium Alloy Sheet by Secondary Regulation of Initial Twin Orientation

Achieving excellent ductility with increased Schmid Factor but decreased direct strain contribution of basal slip in an intergranular misorientation tailored magnesium alloy

Enhanced ductility of Mg–1Zn–0.2Zr alloy with dilute Ca addition achieved by activation of non-basal slip and twinning

Enhanced ductility and strength of Mg-1Zn-1Sn-0.3Y-0.2Ca alloy achieved by novel micro-texture design

Understanding the Deformation Behaviours of Mg Alloys with Dispersed Non-Basal Grain-Embedded Orientation Heterostructures

Ductility Improvement by Twinning and Twin–slip Interaction in a Mg-Y Alloy

The effects of orientation control via tension-compression on microstructural evolution and mechanical behavior of AZ31 Mg alloy sheet

Multiple-twinning induced recrystallization and texture optimization in a differential-temperature-rolled AZ31B magnesium alloy with excellent ductility

Ex-situ EBSD Analysis of Yield Asymmetry, Texture and Twinning Development in Mg–5Li–3Al–2Zn Alloy During Tensile and Compressive Deformation

Improved Ductility of Magnesium Alloys by A Simple Shear Process Followed by Annealing

Modification of Grain Refinement and Texture in AZ31 Mg Alloy by a New Plastic Deformation Method

Achieving Strength-Ductility Balance in AZ31-WE43 Mg Alloys by Symmetric Extrusion-Shear Process at Various Temperatures

Mechanical Behavior and Microstructural Evolution in Rolled Mg-3Al-1Zn-0.5Mn Alloy under Large Strain Simple Shear

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Effect of Original Orientation on Microtexture Evolution of Az31 Mg Alloy

Improving mechanical properties of AZ31 alloy sheets via novel turned-bearing extrusion by introducing shear strain