Abstract:Mg-RE (magnesium-rare earth) binary alloys, such as Mg–Y alloys, usually exhibit weakened texture and excellent plasticity compared with traditional RE-free Mg alloys. However, the weakened texture could lead to a significant decrease in the strength of Mg-RE binary alloys. In this work, the weak-textured Mg–3Y (wt. %) extruded sheet displayed good strength-ductility synergy with a 41% increase in the yield strength and a good ductility similar to the initial sheet via simple pre-twinning and annealing treatment (PT). After PT, the average grain size of the sheet decreased from 11.2 μm to 6.0 μm and 34.2% initial soft texture component (<11–21> //normal direction (ND)) was transformed into the hard texture component (<0001> //transverse direction (TD)). The effect of pre-twinning on deformation mechanisms was systematically investigated by slip trace analysis and activation stress (τ) analysis. Basal slip was the dominant deformation mechanism during the tension of the as-extruded (AE) specimen while pre-twinning promoted the activation of non-basal slip, especially prismatic slip in the PT specimen. The texture transformation and reduced critical resolved shear stress (CRSS) ratio between non-basal slip and basal slip induced by pre-twinning were primarily responsible for the high activity of non-basal slip. The underlying strengthening mechanism and the reason for good ductility were also rationally discussed. The strengthening effect of single grain refinement was relatively lower in the weak-textured Mg–3Y alloy. Texture hardening could effectively improve the effect of fine-grain strengthening. The excellent deformation compatibility between basal slip of parent grains and prismatic slip of twins as well as relatively higher activity of the second-order pyramidal slip was the origin of the good ductility of the PT specimen.

Ductility Improvement by Twinning and Twin–slip Interaction in a Mg-Y Alloy

Twinning Deformation and Yield Asymmetry Improvement of Magnesium Alloys by Free-End Torsion

Deformation mechanism of high ductility Mg-Gd-Mn alloy during tensile process

Study on Deformation Behavior of High Ductility Mg-2Gd-0.5Mn Alloy During Tensile Process

Activation of {1 01¯2} Twinning and Slip in High Ductile Mg–2.0Zn–0.8Gd Rolled Sheet with Non-Basal Texture During Tensile Deformation at Room Temperature

Towards Strength-Ductility Synergy in a Weak-Textured Mg-3Y Extruded Sheet Via Pre-Twinning and Annealing

A Study of High Ductility Mg-2Gd-0.4Zr Magnesium Alloy under Monotonic Tension at Room Temperature

Reasonable Utilization of {10-12} Twin for Optimizing Microstructure and Improving Mechanical Property in a Mg-Gd-Y Alloy

Ductility Enhancement by Activating Non-Basal Slip in Mg Alloys with Micro-Mn

Evolution of deformation mechanisms and their orientation dependence in fine-grained Mg-3Gd during tension

High Ductility of a Mg–Y–Ca Alloy Via Extrusion

Ex-situ EBSD Analysis of Yield Asymmetry, Texture and Twinning Development in Mg–5Li–3Al–2Zn Alloy During Tensile and Compressive Deformation

Critical resolved shear stresses for slip and twinning in Mg-Y-Ca alloys and their effect on the ductility

Towards High Ductility in Magnesium Alloys - the Role of Intergranular Deformation

Effect of Twin and Grain Size Strengthening on Tensile Properties of a Multi-Directionally Impact Forged Mg–Gd–Y Alloy

Twinning and Mechanical Behavior of an Extruded Mg–6Al–3Sn Alloy with a Dual Basal Texture

Quantitative Study on Slip/twinning Activity and Theoretical Critical Shear Strength of Mg Alloy with Y Addition

Improving the Ductility of Mg–Gd–Y–Zr Alloy through Extrusion and a Following Rolling

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Origins of High Ductility Exhibited by an Extruded Magnesium Alloy Mg-1.8Zn-0.2Ca: Experiments and Crystal Plasticity Modeling

Achieving High Ductility and Low In-Plane Anisotropy in Magnesium Alloy Through a Novel Texture Design Strategy