Abstract:Cryogenic rolling experiments have been conducted on the AZ31 magnesium (Mg) alloy sheet with bimodal non-basal texture, which is fabricated via the newly developed equal channel angular rolling and continuous bending process with subsequent annealing (ECAR-CB-A) process. Results demonstrate that this sheet shows no edge cracks until the accumulated thickness reduction reaches about 18.5%, which is about 105.6% larger than that of the sheet with traditional basal texture. Characterization experiments including optical microstructure (OM), X-ray diffractometer (XRD), and electron backscatter diffraction (EBSD) measurements are then performed to explore the microstructure characteristics, texture evolution and deformation mechanisms during cryogenic rolling. Experimental observations confirm the occurrence of abundant {10–12} extension twins (ETs), twin-twin interactions among {10–12} ET variants and {10–12}-{10–12} double twins (DTs). The twinning behaviors as for {10–12} ETs are responsible for the concentration of c-axes of grains towards normal direction (ND) and the formation of transverse direction (TD)-component texture at the beginning of cryogenic rolling. The twinning behaviors with respect to {10–12}-{10–12} DTs are responsible for the disappearance of TD-component texture at the later stage of cryogenic rolling. The involved deformation mechanisms can be summarized as follows: Firstly {10–12} ETs dominate the plastic deformation. Subsequently, dislocation slip, especially basal slip, starts to sustain more plastic strain, while {10–12} ETs occur more frequently and enlarge continuously, resulting in the formation of twin-twin interaction among {10–12} ET variants. With the increasing rolling passes, {10–12}-{10–12} DTs incorporate in the plastic deformation and dislocation slip serves as the major one to sustain plastic strain. The activities of basal slip, {10–12} ETs and {10–12}-{10–12} DTs benefit in accommodating the plastic strain in sheet thickness, which contributes to the improved rolling formability in AZ31 Mg alloy sheet with bimodal non-basal texture during cryogenic rolling.

Multiple-twinning induced recrystallization and texture optimization in a differential-temperature-rolled AZ31B magnesium alloy with excellent ductility

Significantly improvement in formability and ductility of AZ31 Mg alloy by differential temperature rolling

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Improved Mechanical Anisotropy and Texture Optimization of a 3xx Aluminum Alloy by Differential Temperature Rolling

Texture weakening and ductility improvement of Mg-1.1Mn-0.5Al alloy via medium temperature-high reduction rolling: twinning variants selection and dynamic recrystallization mechanism

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Critical Rolling Process Parameters for Dynamic Recrystallization Behavior of AZ31 Magnesium Alloy Sheets.

Texture of AZ31B Magnesium Alloy Sheets Produced by Differential Speed Rolling Technologies

Influence of Bimodal Non-Basal Texture on Microstructure Characteristics, Texture Evolution and Deformation Mechanisms of AZ31 Magnesium Alloy Sheet Rolled at Liquid-Nitrogen Temperature

INFLUENCE OF ROLLING TEMPERATURE ON THE {1011}-{1012} TWINNING IN ROLLED AZ31 MAGNESIUM ALLOY SHEETS

Evolution of Twins and Texture and Its Effects on Mechanical Properties of AZ31 Magnesium Alloy Sheets under Different Rolling Process Parameters

Microstructure and Texture Evolution of Mg-3Zn-1Al Magnesium Alloy During Large-Strain Electroplastic Rolling

Rolling Temperature and Subsequent Annealing on Microstructure, Texture and Mechanical Properties of Consecutive Rolled Mg-2.0zn-0.8gd Alloy

Twinning, dynamic recovery and recrystallization in the hot rolling process of twin-roll cast AZ31B alloy

Dynamic recrystallization, texture and mechanical properties of high Mg content Al–Mg alloy deformed by high strain rate rolling

Microstructure and Texture Evolution of AZ31 Magnesium Alloy Thin Sheet Processed by Hot‐Rolling–Shearing–Bending

Twinning, Grain Orientation, and Texture Variations in Mg Alloy Processed by Pre-Rolling

Microstructure and Texture Evolution of AZ31 Magnesium Alloy During Rolling

Achieving High Ductility and Low In-Plane Anisotropy in Magnesium Alloy Through a Novel Texture Design Strategy

Texture Evolution of AZ31 Magnesium Alloy Sheets During Warm Rolling

Effect of Differential Speed Rolling on the Room and Elevated Temperature Tensile Properties of Rolled AZ31 Mg Alloy Sheets