Abstract:In this study, a novel technique of consecutive multi-pass cooperative lowered-temperature rolling (CMCLR) was proposed for the first time, with the purpose of preparing high performance wrought magnesium alloys. Based on this, a highly ductile magnesium alloy sheet could be effectively produced from ingot. The corresponding microstructure could directly evolve from coarse dendrites to equiaxed grains with an average size of similar to 5 mu m, which was attributed to the intense dynamic recrystallization (DRX) during isothermal deformation. The equivalent strain gradually decreased from the surface to the interior and edge of the rolled sheet due to the anisotropic plastic deformation. Instead, the temperature of the core of the sheet was slightly higher than that of the surface due to the deformation heat effect. The basal texture in the RD-TD plane generally weakened in the form of the splitting of basal texture toward the RD and the broadening of basal plane away from the pole center due to texture randomization dominated by DRXed grains. The exceptional ductility of more than 28.7% together with acceptable ultimate tensile strength of not less than 267 MPa was ascribed to the progressive work hardening as a result of seamless switching of multiple deformation modes, i.e., basal dislocation-slip-mediated deformation was preferentially operated and then was substituted by twinning-controlled deformation and non-basal dislocation-slip-dominated deformation. The selection of {10 (1) over bar2} twin variants agreed well with geometrical compatibility factor (m') criterion instead of Schmid's law. The activated twin variants nearly engulfed the whole parent grains for the sake of preserving compatible deformation continuity at ambient temperature, giving rise to the formation of TD-split texture. Comparatively, the {10 (1) over bar2} twinning could randomize the basal texture via reorienting grain orientations which in turn facilitated the reactivation of dislocation slip systems in the case of high temperature deformation.

Texture weakening and ductility improvement of Mg-1.1Mn-0.5Al alloy via medium temperature-high reduction rolling: twinning variants selection and dynamic recrystallization mechanism

Effect of Al addition and rolling reduction on microstructure and texture evolution of Mg–3Sn alloy during high-speed rolling

Multiple-twinning induced recrystallization and texture optimization in a differential-temperature-rolled AZ31B magnesium alloy with excellent ductility

Non-basal Slips Mediated Dynamic Recrystallization Promote Synergistic Strengthening and Toughening of Centrifugal Casting Mg–1.1Mn–0.5Al Alloy via High Strain Rolling

Twinning-mediated Texture Weakening in a Basal-Textured Mg-6Al-1Zn (mass%) Alloy Sheet by a Novel Cold-Sample Rolling Method

Twinning-Assisted Static Recrystallization and Texture Evolution in A Mg-Gd-Y-Zr Alloy

Dynamic recrystallization, texture and mechanical properties of high Mg content Al–Mg alloy deformed by high strain rate rolling

Evolution of Twins and Texture and Its Effects on Mechanical Properties of AZ31 Magnesium Alloy Sheets under Different Rolling Process Parameters

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Enhanced rollability of Mg alloys by directly activated { 10 1 ̄ 2 } twinning during asymmetric rolling: Experiments and finite element analysis

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

Insights into the evolution of texture and mechanical properties during warm rolling and annealing of Mg–2Zn-0.5Ca alloy

Dynamic recrystallization behaviors of high Mg alloyed Al-Mg alloy during high strain rate rolling deformation

Dynamic precipitation and twinning-induced dynamic recrystallization in Mg–6Al–3Sn–1Zn alloy during multi-pass high-speed rolling

Twinning, Grain Orientation, and Texture Variations in Mg Alloy Processed by Pre-Rolling

Twinning Behavior of a Strongly Basal Textured AZ31 Mg Alloy During Warm Rolling

Dramatic Improvement of Formability in Mg-3Al-1Sn-0.5Ca-0.1Sm Alloy Via Mn Microalloying Combined with High Temperature Rolling

Microstructure, Texture and Mechanical Properties Evolution of Pre-Twinning Mg Alloys Sheets During Large Strain Hot Rolling

Critical Rolling Process Parameters for Dynamic Recrystallization Behavior of AZ31 Magnesium Alloy Sheets.

Achieving High Ductility and Low In-Plane Anisotropy in Magnesium Alloy Through a Novel Texture Design Strategy

Microstructure, Mechanical Properties and Texture Evolution of Mg–Al–Zn–La–Gd–Y Magnesium Alloy by Hot Extrusion and Multi-Pass Rolling