Abstract:Suspension effect poses a big threat to the integrity and safety of corroded pipelines. In this work, a finite element (FE) based multi-physics field coupling model was developed to determine the mechano-electrochemical (M-E) interaction at an external corrosion defect on a suspended X100 steel pipe and predict its failure pressure. Theoretical calculations were used for model validation. Parameter effects including the defect location on the pipe, geometry of the defect, suspension length and pipe burial depth were determined. Results demonstared that, generally, the M-E effect at corrosion defect caused an increased stress concentration and anodic current density (i.e., corrosion rate), decreasing the failure pressure of the pipeline. The effect became more apparent when the pipe was in suspension. Both the stress and the anodic current density at the corrosion defect were dependent on the defect geometry, especially the defect depth. When the depth was up to 40% of pipe wall thickness, the von Mises stress exceeded the yield stress of the steel, causing local plastic deformation. A critical defect length of <math>20Dt</math> (D is the outer diameter of the pipe and t is pipe wall thickness) existed, below which the von Mises stress and the anodic current density at the corrosion defect increased with increased defect length. When the defect length exceeded the critical value, the effect was not obvious. An increased suspension length of the pipe would elevate the local stress and anodic current density at the corrosion defect, reducing the failure pressure of the pipe. A critical pipe burial depth of 2.5 m was identified, exceeding which the failure pressure of the pipe decreased rapidly with the increased burial depth. When the burial depth was smaller than 2.5 m, the effect was marginal. The location of the corrosion defect on the pipe did not affect the local stress, anodic current density and failure pressure at an appreciable level, and could be ignored in defect assessment on suspended pipelines.

In-situ Electrochemical Testing and Fluid Dynamics Simulation of Pipeline Defects under Flow Accelerated Corrosion

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Study on the effect of corrosion defects on VIV behavior of marine pipe using a new defective pipe element

Study on the localized flow-accelerated corrosion of EH32 steel based on wire beam electrodes and EIS measurements

Flow-Accelerated Corrosion Damage in a Steam Pipe Girth Weld

Effects of fluid dynamics Parameters on flow-accelerated corrosion at elbow of carbon steel pipeline

Effect of Fusion Boundary Microstructure on Flow-Accelerated Corrosion Cracking

Investigation by numerical modeling of the mechano-electrochemical interaction of circumferentially aligned corrosion defects on pipelines

The Effect of Flowing Velocity and Impact Angle on the Fluid-Accelerated Corrosion of X65 Pipeline Steel in a Wet Gas Environment Containing CO2

Numerically Investigating the Influence of Local Flow Behaviors on Flow-Accelerated Corrosion Using Two-Fluid Equations

Pipeline condition assessment and finite element modeling of mechano-electrochemical interaction between corrosion defects with varied orientations on pipelines

Flow-Induced Corrosion Simulation on a Plate by Finite Element Methods

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Assessment by finite element modelling of the mechano-electrochemical interaction at corrosion defect on elbows of oil/gas pipelines

Characterization of Flow-Accelerated-corrosion of Pressure Piping Welded Joints

Finite element modeling of local corrosion accelerated by the mechano-electrochemical coupling effect at defects on pipelines under combined effects of internal pressure and axial applied stress

Integrity Assessment of the Pipelines Containing an Isolated Corrosion Pit

Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction

Experimental and Numerical Analysis of the Impact of Corrosion on the Failure Pressure of API 5L X65 Pipeline

Safety and reliability assessment of external corrosion defects assessment of buried pipelines—soil interface: A mechanisms and FE study

Development of a finite element model for simulation and prediction of mechanoelectrochemical effect of pipeline corrosion