Study on the localized flow-accelerated corrosion of EH32 steel based on wire beam electrodes and EIS measurements

Qiliang Zhang,Wanbin Chen,Peinan Liang,Wanheng Jiang,Jiahua Su,Yi Huang,Yunze Xu

DOI: https://doi.org/10.1016/j.mtcomm.2024.111147

IF: 3.8

2024-12-01

Materials Today Communications

Abstract:This study investigated the flow-accelerated corrosion (FAC) behaviour of EH32 steel using a submerged impingement jet system. The dynamic development process of FAC was monitored in real-time by combining wire beam electrodes (WBE) and EIS measurements. The distribution of the flow field and mass transfer rates were calculated through CFD simulation. The results show that the WBE technique effectively visualizes the dynamic development process of FAC under non-uniform flow fields. Inhomogeneous distribution of the flow field and variations in mass transfer rates were identified as the primary factors influencing the early stages of FAC development. An accumulation of anolyte in the centre of the electrode under the influence of the flow field led to the evolution of this region into the main anodic area, fostering macro-cell corrosion between the surrounding region. In the later stages of FAC, the rust layer emerged as a critical factor influencing the FAC behaviour. Discrepancies in wall shear stress and corrosion across various areas result in diverse localized characteristics of the rust layer on the electrode surface. The inhibition of the mass transfer process by the rust layer mitigates macro-cell corrosion. The impact of the flow field and the rust layer on the transfer of the anolyte is the primary factor driving the development of "flow mark" corrosion patterns in the central area and pitting corrosion patterns in the edge area.

materials science, multidisciplinary