Fatigue Fracture Surface Analysis and Fatigue Life Estimation of Corroded Steel Wires

Xiang-long ZHENG,Xu XIE,Xiao-zhang LI,Jian-min HU,Wen-zhi SUN

DOI: https://doi.org/10.3969/j.issn.1006-3897.2017.04.010

2017-01-01

Abstract:In order to explore the fatigue performance and fatigue fracture mechanism of corroded high-tensile steel wires and provide the experimental basis for fatigue life evaluation of corroded wires in view of fracture mechanics theory,two types of corroded wires were investigated through fatigue tests under different stress amplitudes.One type of the steel wire was sampled from the hangers of a floating-system arch bridge which has served for more than 10 years,and the other type was derived from the steel wires with a treatment of artificial accelerate corrosion.Through the observation of scanning electron microscopic,the fracture surface morphology and the fatigue failure process of corroded wires were analyzed and the crack initiation pitting sizes of the two types of corroded wires were comparatively discussed.The initial-crack stress intensity factors and the residual fracture toughness of the two types of corroded wires were analyzed and compared with the existing indexes of the fatigue threshold and the fracture toughness of steel wires.The S-N curves of corroded wires was fitted by the three-parameter formula and S-N curves of different corroded wires were compared as well.Moreover,the linear elastic fracture mechanics approach was employed to analyze the characteristics of the fatigue life under high stress amplitudes.The results show that the fatigue performance of the steel wires declines with the increase of corrosion degree.Multi-source cracks and irregular crack propagation are easily induced when corrosion pits are dense-distributed.The critical condition for a main crack to initiate mainly depends on the fatigue crack propagation threshold /△Kth.The inflection point of the S-N curve arises at the low stress range of corroded steel wires,in correspondence with the fitting rules of the three-parameter formula.Owing to a large proportion of fatigue crack propagation life,the fatigue crack propagation life S-N curves of the corroded steel wires can well reflect the average fatigue behavior in medium fatigue life region by assuming a certain initial crack size.