Abstract:In order to explore the fatigue performance and fatigue fracture mechanism of corroded high-tensile steel wires and provide the experimental basis for fatigue life evaluation of corroded wires in view of fracture mechanics theory,two types of corroded wires were investigated through fatigue tests under different stress amplitudes.One type of the steel wire was sampled from the hangers of a floating-system arch bridge which has served for more than 10 years,and the other type was derived from the steel wires with a treatment of artificial accelerate corrosion.Through the observation of scanning electron microscopic,the fracture surface morphology and the fatigue failure process of corroded wires were analyzed and the crack initiation pitting sizes of the two types of corroded wires were comparatively discussed.The initial-crack stress intensity factors and the residual fracture toughness of the two types of corroded wires were analyzed and compared with the existing indexes of the fatigue threshold and the fracture toughness of steel wires.The S-N curves of corroded wires was fitted by the three-parameter formula and S-N curves of different corroded wires were compared as well.Moreover,the linear elastic fracture mechanics approach was employed to analyze the characteristics of the fatigue life under high stress amplitudes.The results show that the fatigue performance of the steel wires declines with the increase of corrosion degree.Multi-source cracks and irregular crack propagation are easily induced when corrosion pits are dense-distributed.The critical condition for a main crack to initiate mainly depends on the fatigue crack propagation threshold /△Kth.The inflection point of the S-N curve arises at the low stress range of corroded steel wires,in correspondence with the fitting rules of the three-parameter formula.Owing to a large proportion of fatigue crack propagation life,the fatigue crack propagation life S-N curves of the corroded steel wires can well reflect the average fatigue behavior in medium fatigue life region by assuming a certain initial crack size.

Ultra-low Cycle Fatigue Properties and Fracture Mechanism of Corroded Structural Steel

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

Fatigue Fracture Surface Analysis and Fatigue Life Estimation of Corroded Steel Wires

Ultra-low Cycle Fatigue Fracture Initiation Life Evaluation of Thick-Walled Steel Bridge Piers with Microscopic Damage Index under Bidirectional Cyclic Loading

A Modified Coffin-Manson Model for Ultra-Low Cycle Fatigue Fracture of Structural Steels Considering the Effect of Stress Triaxiality

Study on Ultra‐low Cycle Fatigue Fracture of Thick‐walled Steel Bridge Piers

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

A Deformation History-Based Approach for Ultra-Low Cycle Fatigue Damage Evaluation of Steel Structures

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Monotonic and fatigue behavior of steel-concrete composite beams subjected to corrosion

Behavior of Corroded Thin-Walled Concrete-Filled Steel Tubular Stub Columns

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Fatigue Behavior of High-Performance Steel Beams Subjected to Different Corrosion Conditions

The correlation between prior fatigue damage and remaining creep properties in a high chromium steel welded joint

Fatigue Life Evolution of Steel Wire Considering Corrosion-Fatigue Coupling Effect: Analytical Model and Application

A study of ultra-low cycle fatigue failure based on a fracture strain energy model