Abstract:Suspension effect poses a big threat to the integrity and safety of corroded pipelines. In this work, a finite element (FE) based multi-physics field coupling model was developed to determine the mechano-electrochemical (M-E) interaction at an external corrosion defect on a suspended X100 steel pipe and predict its failure pressure. Theoretical calculations were used for model validation. Parameter effects including the defect location on the pipe, geometry of the defect, suspension length and pipe burial depth were determined. Results demonstared that, generally, the M-E effect at corrosion defect caused an increased stress concentration and anodic current density (i.e., corrosion rate), decreasing the failure pressure of the pipeline. The effect became more apparent when the pipe was in suspension. Both the stress and the anodic current density at the corrosion defect were dependent on the defect geometry, especially the defect depth. When the depth was up to 40% of pipe wall thickness, the von Mises stress exceeded the yield stress of the steel, causing local plastic deformation. A critical defect length of <math>20Dt</math> (D is the outer diameter of the pipe and t is pipe wall thickness) existed, below which the von Mises stress and the anodic current density at the corrosion defect increased with increased defect length. When the defect length exceeded the critical value, the effect was not obvious. An increased suspension length of the pipe would elevate the local stress and anodic current density at the corrosion defect, reducing the failure pressure of the pipe. A critical pipe burial depth of 2.5 m was identified, exceeding which the failure pressure of the pipe decreased rapidly with the increased burial depth. When the burial depth was smaller than 2.5 m, the effect was marginal. The location of the corrosion defect on the pipe did not affect the local stress, anodic current density and failure pressure at an appreciable level, and could be ignored in defect assessment on suspended pipelines.

Development of a finite element model for simulation and prediction of mechanoelectrochemical effect of pipeline corrosion

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

A finite element based model for prediction of corrosion defect growth on pipelines

Assessment by finite element modelling of the mechano-electrochemical interaction at double-ellipsoidal corrosion defect with varied inclinations on pipelines

Pipeline condition assessment and finite element modeling of mechano-electrochemical interaction between corrosion defects with varied orientations on pipelines

Investigation by numerical modeling of the mechano-electrochemical interaction of circumferentially aligned corrosion defects on pipelines

Finite element modeling of corrosion defect growth and failure pressure prediction of pipelines

Finite element modeling of local corrosion accelerated by the mechano-electrochemical coupling effect at defects on pipelines under combined effects of internal pressure and axial applied stress

Assessment by finite element modelling of the mechano-electrochemical interaction at corrosion defect on elbows of oil/gas pipelines

Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction

Assessment of the local mechano-electrochemical effect on pipeline defects by 2D and 3D finite element models

Study of mechano-electrochemical model: a numerical and experimental approach

Effects of external corrosion defect growth on wall pipeline under internal pressure and various defect sizes with mechano‐electrochemical interaction

A Coupled Electro-Chemo-Mechanical Model for the Stress Corrosion Cracking Prediction of Stainless Steel in High-Temperature Water

Numerical investigation of the mechano-electro-chemical effect of X100 buried pipelines with pre-existing corrosion defects

Assessment by finite element modeling of the interaction of multiple corrosion defects and the effect on failure pressure of corroded pipelines

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

A Corrosion Cracking Mechanism-Based Model with Molten Salt Corrosion Damage Coupling the Effect of Chloride Impurity and Plastic Deformation

Finite element modeling of hydrogen atom diffusion and distribution at corrosion defect on aged pipelines transporting hydrogen

Localized corrosion behavior on a heterogeneous surface involving multicomponent reactive transport and morphology evolution

Analytical prediction of failure pressure for pipeline with long corrosion defect