Abstract:In this study, tungsten and steel were successfully bonded utilizing hot isostatic pressing diffusion bonding with a Ni-Si-B interlayer. The interfacial structures and formation mechanisms of joints with interlayers of various thicknesses were systematically investigated. The results indicated that the interfacial structure of a joint with a thin (0.8 μm) Ni-Si-B interlayer is a W/Fe-W inter-metallic compound (IMC) reaction layer/(Fe,Ni)ss diffusion layer/steel structure, where through cracks appear at the interface of the W/reaction layer, leading to poor shear strength. As the interlayer thickness increases (3.2 to 22.9 μm), the brittle Fe-W IMC no longer appears and the interfacial structure is a W/Ni-W IMCs reaction layer/(Ni,Fe)ss diffusion layer/steel structure. When the interlayer thickness is 3.2 μm, there are many large voids in the diffusion layer. When the interlayer thickness increases to 5.3 μm, the most compact interfacial structure can be obtained with the maximum bonding strength of 363.5 MPa. However, when the interlayer thickness increases further to 12.6 and 22.9 μm, many voids appear in the reaction layer, leading to a decrease in bonding strength. The formation mechanism of a joint with a thin (0.8 μm) interlayer is a purely solid-solid reaction without the generation of a liquid phase. When the interlayer thickness is large (3.2 to 22.9 μm), the formation process of joints includes three stages: solid-solid reaction, remaining interlayer liquefaction, and solid-liquid reaction. Electron probe microanalysis results reveal that the melting-point depressant element Si is segregated in the reaction layer or diffusion layer depending on the interlayer thickness, which is precisely controlled by the staged formation mechanism of the joints.

Characterization of Diffusion Bonded W/Steel Joint by Electroplating-Assisted Hot Isostatic Pressing

Research on Be/CuCrZr Bonding by Hot Isostatic Pressing at Intermediate Temperature

Interfacial microstructures, residual stress and mechanical analysis of hot isostatic pressing diffusion bonded joint of 93W–4.9Ni–2.1Fe alloy and 30CrMnSiNi2A steel

Interfacial structure and formation mechanism of tungsten/steel HIP diffusion bonding joints using Ni interlayer

Characterization of Ductile Nano-Tic Dispersed V4Cr4Ti/RAFMs Solid Diffusion Joint for Nuclear Fusion Reactor Application

Effect of Composite Interlayer on Bonding Quality of W and Steel HIP Joint

Effect of holding time on the microstructure and strength of tungsten/steel joints by HIP diffusion bonded using a Cu interlayer

Microstructure, properties, and formation mechanisms of tungsten/steel hot isostatic pressing diffusion bonding joint utilizing a Ni-Si-B interlayer

Tungsten/steel diffusion bonding using Cu/W–Ni/Ni multi-interlayer

Effect of bonding process on the microstructures and strength of W/steel joints with a W-Cu-Ni interlayer

Investigation of tungsten/steel diffusion bonding with Ni–Fe cladding on tungsten substrate

Interface characterization of Be/CuCrZr joints by hot isostatic pressing bonding

Hot Isostatic Pressing Diffusion Bonding and Interface Residual Stress Analysis of CuCr1Zr Alloy and 25Cr2Ni4MoV Steel

Microstructure, residual stresses and mechanical properties of diffusion bonded tungsten–steel joint using a V/Cu composite barrier interlayer

Interfacial microstructure and strengthening mechanism of W/steel diffusion bonding joint using a porous NiFeWss interlayer prepared by in-situ reduction

Effect of Ti Interlayer on the Bonding Quality of W and Steel HIP Joint

On the use of CoCrFeNi high entropy alloy as a new interlayer for achieving high strength diffusion bonded tungsten/steel joint

Investigation of tungsten/MA956 steel diffusion bonding with an Nb/Ni composite interlayer

Effect of holding time on the microstructure and strength of tungsten/ferritic steel joints diffusion bonded with a nickel interlayer

Microstructure and mechanical properties of diffusion bonded joints between tungsten and F82H steel using a titanium interlayer

Stable bonding of W and ODS steel fabricated by TLP diffusion technology through inserting a novel composite interlayer Zr/Cu