Interfacial microstructures, residual stress and mechanical analysis of hot isostatic pressing diffusion bonded joint of 93W–4.9Ni–2.1Fe alloy and 30CrMnSiNi2A steel

Wensheng Liu,Qingqing Sheng,Yunzhu Ma,Qingshan Cai,Jianning Wang,Yang Liu

DOI: https://doi.org/10.1016/j.fusengdes.2020.111602

IF: 1.905

2020-07-01

Fusion Engineering and Design

Abstract:Circular sleeves of 93W–4.9Ni–2.1Fe alloy (W–Ni–Fe) and 30CrMnSiNi2A steel were connected by a hot isostatic pressing (HIP) diffusion bonding method. W–Ni–Fe/steel joint mock–up with a dimension of 30ID mm × 50OD mm × 50H mm was successfully fabricated. Metallographic analysis with field–emission scanning electron microscope (FE–SEM) revealed the diffusion zone of the joint interface consists of W/steel diffusion layer and Ni–Fe/steel diffusion layer. Electron probe microanalysis (EPMA) and X–ray diffraction (XRD) analysis exhibits the brittle intermetallic phase Fe7W6 is formed at the W/steel diffusion zone. The average tensile strength of ∼310.5 MPa along with 8.6 % elongation has been obtained for the HIP diffusion couple and the fracture occurs predominantly in W–Ni–Fe near the joint interface because of the thermal stress concentration. Thermally induced stresses and strains in the W–Ni–Fe/steel HIP joint were analyzed using finite element method (FEM). The results reveal that the peak equivalent residual stress on entire joint is located at the W–Ni–Fe side near the interface close to the free surface. Meanwhile, the steel substrate releases the residual stress by generating plastic deformation.

nuclear science & technology