Abstract:Selective laser melting (SLM) offers unprecedented advantages in manufacturing complex components used in nuclear reactors, and thus has promising application in the nuclear power industry. The compatibility of printed materials with typical reactor coolant should be carefully investigated as the printed materials possess unique microstructure features (e.g. columnar grain, dislocation cell and inclusion) which would inevitably affect the performance. In this work, the stress corrosion cracking (SCC) susceptibility of selective laser melted (SLMed) 304L stainless steel (SS) was evaluated in high-temperature hydrogenated water through slow strain rate tensile test and compared with two wrought 304 SSs. Interestingly, the SLMed 304L SS showed much lower SCC susceptibility than the two wrought 304 SSs, and this finding was mainly ascribed to its optimized composition. From the aspect of corrosion, the intergranular oxidation resistance of SLMed 304L SS is significantly improved due to the reduced contents of Si and Mn. In addition, the high dislocation density in SLMed 304L SS can accelerate the diffusion of solute atoms, thus further enhancing the resistance to intergranular oxidation and promoting the precipitation of oxide inside the crack which barricades the ingress of corrosive media. As for the mechanical aspect, under the combined effects of dislocation cells and nano-oxide inclusions, the SCC initiation can be alleviated as the dislocation motion in the grain matrix is hindered and planar slip is suppressed. Therefore, the optimized chemical composition and printed microstructure render this SLMed 304L SS more resistant to SCC initiation.

Insights into the Superior Stress Corrosion Cracking Resistance of FeCrAl Alloy in High Temperature Hydrogenated Water: the Critical Role of Grain Boundary Oxidation

On the Stress Corrosion Crack Initiation Behaviour of Alloy 800 in High-Temperature Hydrogenated Water

Insights into Oxidation and Nitridation of Alumina-Forming FeCrAl Alloy after Supercritical Water Exposure: Effect of Pre-Corrosion on High-Temperature Damage Behavior

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Improving the Corrosion Resistance of FeCrAl Alloy in High Temperature Hydrogenated Water Through Gaseous Pre-Oxidation

Corrosion Behavior of FeCrAl Alloy and NiCr Coated Zircaloy-4 in Hydrogenated Water

Corrosion Behavior of Ultrafine-Grained CoCrFeMnNi High-Entropy Alloys Fabricated by High-Pressure Torsion

Effect of Elements on Hydrogen Pickup and Corrosion Behavior of ZrFeCr Alloys in 500°C Steam

The SCC Initiation Behavior of Alloy 600 During the Transition of Hydrogenated/oxygenated Water Condition at Evaluated Temperature

Effect of dissolved oxygen and hydrogen on the stress corrosion cracking behavior of alloy 600 in high temperature water

Uniform Corrosion Behavior of FeCrAl Alloys in Borated and Lithiated High Temperature Water

Hydrogen-enhanced oxidation of ferrite phase in stainless steel cladding and the contribution to stress corrosion cracking in deaerated high temperature water

Intergranular corrosion of Ni-30Cr in high-temperature hydrogenated water after removing surface passivating film

Incipient Corrosion of FeCrAl Alloys in H3BO3- and LiOH-containing Pure Water at 360 °C and 18.5 MPa

Corrosion of FeCrAl-1Nb Alloy in Deaerated Water at 290 ℃ and 7mpa: the Oxidation Behavior of Grain Boundary

Corrosion of FeCrAl-1Nb alloy in Deaerated Water at 290 °C and 7MPa: The Oxidation Behavior of Grain Boundary

Influence of Alloyed Sc and Zr, and Heat Treatment on Microstructures and Stress Corrosion Cracking of Al–Zn–Mg–Cu Alloys

The Effect of Grain Boundary Structure on the Intergranular Degradation Behavior of Solution Annealed Alloy 690 in High Temperature, Hydrogenated Water

The Environmental Degradation Behavior of FeNiMnCr High Entropy Alloy in High Temperature Hydrogenated Water

Atomic Insights into the Corrosion Behavior of Fe-Cr Alloys in Supercritical CO2 Environment

Insights into the Stress Corrosion Cracking Resistance of a Selective Laser Melted 304L Stainless Steel in High-Temperature Hydrogenated Water