THE MATERIAL DESIGN OF CR-BASED BINARY ALLOYS AND ITS CORROSION BEHAVIOR ANALYSIS FOR ACCIDENT-TOLERANT FUEL DEVELOPMENT
John Andrew Kane JOVELLANA,Huilong YANG,Bo LI,Lijuan CUI,Quanqiang SHI,Ziqi WEI,Sho KANO,Hiroaki ABE
DOI: https://doi.org/10.1299/jsmeicone.2023.30.1353
2023-01-01
The Proceedings of the International Conference on Nuclear Engineering (ICONE)
Abstract:As a severe consequence of the Fukushima Daiichi Nuclear Accident in 2011, the hydrogen explosions are attributed to zirconium oxidation with steam surrounding the fuel claddings at high temperatures. This event encouraged the development of accident-tolerant fuels (ATF) worldwide. Active ATF research studies currently focus on using a Cr-based metal coating to protect the current Zr alloy tubing. However, concerning the properties of Cr like brittleness, materials modifications could be desirable that offer good performance in fabrication and reactor operations. Alloying of Cr is expected for possible improvements, and the desirable alloying elements are expected to maximize corrosion resistance along with sufficient mechanical properties, acceptable irradiation resistance, and sufficient protection at high temperatures. The objectives of this work are to synthesize Cr-based alloys and to clarify corrosion kinetics and related microstructure evolutions. Cr-based binary alloys with Fe, Al, and Sn were fabricated using vacuum arc melting, followed by heat treatment and surface preparation. The specimens were subjected to batch autoclave corrosion in distilled water at 360°C and 17.8 MPa for duration up to 56 days. The corrosion rates were determined by measuring the weight gains of the samples and fitted to the oxidation law. It was observed that Cr-0.5Sn and Cr-2Al have similar kinetic corrosion performance compared to pure Cr. Cr-2Fe and Cr-7Fe showed similar kinetic corrosion performance but slightly higher corrosion rates. Kinetic behaviors of Cr-3Sn and Cr-9.5Al did not follow the expected exponential law. Microscopic observations also indicate the uniform corrosion in the most of samples. Exceptions are Cr-3Sn and Cr-9.5Al which exhibited Sn dissolution resulting in surface void formation, and redistribution of Al, respectively. TEM observations and GIXRD analysis indicated formation of oxide layers such as Cr2O3, Fe3O4, Fe2O3, SnO, SnO2 and Al2O3 in the specimens. By comparing with Zr alloys, significant improvement in corrosion behavior was evident in Cr and its binary alloys.