Abstract:FeCrAl alloy is one of the potential candidates of structural materials due to its high strength, low radiation swelling and good oxidation resistance for the application of lead-cooled fast reactors (LFRs). Particularly, FeCrAl alloy can form protective Al-containing oxide scales after exposure to liquid oxygen-rich Pb and lead-bismuth eutectic (LBE) at 400-800 °C, showing better performance than traditional commercial stainless steels such as T91, 316L and 15-15Ti. Given the possibility that oxygen in liquid metal could be consumed and not be supplied timely in some quasi-static regions of the actual coolant circuit, to figure out the corrosion behavior of FeCrAl alloy in oxygen-depleted LBE is necessary. In this work, the commercial FeCrAl alloy was exposed to static liquid LBE with 10 -9 wt.% oxygen concentration at 600 °C for up to 5000 h, and the surface and cross-sectional morphology of the samples was characterized and analysed. It is found that FeCrAl alloy underwent severe dissolution corrosion, and the maximum penetration depth of LBE reached 161.4 μm after the test for 5000 h; PbBi infiltrated into alloy matrix along the GBs and selectively leached Al from the affected grains. Besides, an interesting discovery is the Cr-rich thin layer at LBE/matrix interface and Ni 3 Al precipitates in LBE penetration front which should be attributed to the deposition of impurity elements dissolved in liquid LBE during the cooling process.

Incipient Corrosion of FeCrAl Alloys in H3BO3- and LiOH-containing Pure Water at 360 °C and 18.5 MPa

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Influences of Fluorine on Corrosion Behavior of FeCrAl Alloy in Lithiated/borated Water at 360 °C/18.5 MPa

Uniform Corrosion Behavior of FeCrAl Alloys in Borated and Lithiated High Temperature Water

Corrosion of Zircaloy-4, Zr-1Nb and FeCrAl Alloys in Deaerated Water at 330 °C and 14 MPa: Superior Corrosion Resistance and Corrosion Mechanism of FeCrAl Alloy by Experiments and Molecular Dynamics Simulations

Dissolution corrosion of FeCrAl alloy exposed to oxygen-depleted lead-bismuth eutectic containing Ni impurities at 600 °C

Corrosion Behavior of FeCrAl Alloy and NiCr Coated Zircaloy-4 in Hydrogenated Water

Microstructure of FeCrAl Thin Film Composed of Nanocrystals Deposited on Zr Alloy and Their Corrosion Behavior under Water Steam Atmosphere.

Spin-polarized DFT calculations of elemental effects on hydrogen atom adsorption on FeCrAl (110) surface

The Elemental Effects on the H2 Dissociative Adsorption on FeCrAl (110) Surface

Corrosion Behavior and Mechanisms of Al2O3 and Mo Coated Zircaloy-4 in High-Temperature Lithiated Water

Xe20+ ions irradiation and autoclave corrosion coupled with steam oxidation behaviors of FeCrAlMoSiY-coated Zr claddings

Corrosion Behaviors of FeCrAl Alloys Exposed to Oxygen-Saturated Static Lead Bismuth Eutectic at 550 °C

Improving the Corrosion Resistance of FeCrAl Alloy in High Temperature Hydrogenated Water Through Gaseous Pre-Oxidation

Investigation on the Oxidation and Corrosion Behaviors of FeCrZr Alloy As a Protective Material for Zr Cladding

Insights into Oxidation and Nitridation of Alumina-Forming FeCrAl Alloy after Supercritical Water Exposure: Effect of Pre-Corrosion on High-Temperature Damage Behavior

Corrosion of FeCrAl Alloys Used As Fuel Cladding in Nuclear Reactors

Microstructural Evolution of the Cr/FeCrAl Coated Zircaloy-4 under Simulated PWR and High-Temperature Steam Oxidation Environments

Early corrosion behaviour of irradiated FeCrAl alloy in a simulated pressurized water reactor environment

Corrosion behavior of Cr-coated zirconium alloy cladding in LiOH/H3BO3-containing water at 360 °C

Corrosion Behavior of Nb-doped FeCrAl Alloy in 500°C Steam