Abstract:The multilayer graphene (MLG) reinforced WC-10Ni 3 Al cemented carbide was prepared by microwave sintering. The effects of the sintering temperature and MLG content on the microstructure and mechanical properties of the WC-10Ni 3 Al cemented carbide were investigated. The promotion effect and strengthening mechanism of MLG on WC-10Ni 3 Al by microwave sintering were explored. The tribological properties of WC-10Ni 3 Al and Ti6Al4V(TC4) were studied, and the wear mechanism of WC-10Ni 3 Al was revealed. The experiment result show that the WC-10Ni 3 Al-0.5 wt.% MLG sample sintered at 1450°C had its greatest mechanical properties with a relative density of 96.9%, hardness of 1430 HV, flexural strength of 1410 MPa and fracture toughness of 15.7 MPa·mm 1/2 , which were 4.2%, 12.2%, 24.4%, and 29.6% greater than those of the sample without MLG added, respectively. The reinforcing and toughening mechanisms of adding MLG in WC-10Ni 3 Al samples consist of fine crystal strengthening, crack bridging and deflection, MLG pulling out and bridging. The results of friction experiment show that the friction coefficient and wear rate of the WC-10Ni 3 Al samples were lower than those of YG8 (WC-8 wt. % Co cemented carbide). The WC-10 Ni 3 Al-0.5 wt.% MLG sample obtained the lowest friction coefficient of 0.35 and the lowest wear rate of 1.69 × 10 -5 mm 3 N -1 m -1 . A stable solid lubrication film was produced on the friction surface of the WC-10Ni 3 Al samples, which was conducive to reducing the breakage and wear of WC grains. MLG can enhance the stability of solid lubrication film and reduce its friction coefficient.

Tribological performance of binderless tungsten carbide reinforced by multilayer graphene and SiC whisker

Mechanical properties of binderless tungsten carbide enhanced via the addition of ZrO2-20 wt% Al2O3 composite powder and graphene nanosheets

Determination of Microstructure and Mechanical Properties of Ceramics Bonded Tungsten Carbide Doped with Hybrid Graphene/sicw

Preparation and Properties of Multilayer Graphene Reinforced Binderless TiC Nanocomposite Cemented Carbide Through Two-Step Sintering

A Review on Binderless Tungsten Carbide: Development and Application

Excellent Tribological Properties and Unique Wear-Resistance Mechanism of Binderless Tungsten Carbide Prepared Via Two-Step Oscillatory Pressure Sintering

Effect of the additive multilayer graphene on the enhanced tribological properties of ultra-coarse WC-Co cemented carbides

High-hard and High-Tough WC-TiC-Co Cemented Carbide Reinforced with Graphene

Hybrid Multilayer Graphene and SiC Whisker Reinforced TiB2 Based Nano-Composites by Two-Step Sintering

Enhanced mechanical and tribological properties of oscillatory pressure sintered WC–GNPs composites

Influence of binder systems on sintering characteristics, microstructures, and mechanical properties of PcBN composites fabricated by SPS

Preparation of WC@graphene reinforced titanium diboride‐based composite ceramic materials fabricated via SPS

Simultaneously enhancing the toughness and strength of cemented TiB 2 nanocomposites through doping SiC whisker and graphene

Tailoring Mechanical and Tribological Properties of Oscillatory Pressure Sintered Binderless WC Ceramics with Expanded Graphite Addition

Microstructure, mechanical and friction-wear properties of SiC-WC composite with Al and C as sintering aids

Tribological behavior and mechanism of h-BN modified copper metal matrix composites paired with C/C–SiC

Investigation of microstructure and tribological performances of high-fraction TiC/graphene reinforced self-lubricating Al matrix composites

Mechanical and tribological properties of WC particles reinforced Cu-20Zn matrix composites

Study on interface modification and tribological properties of MCMB-SiC self-lubricating composites

Microstructure, mechanical and tribological properties of multilayer grapheme reinforced WC-10Ni 3 Al prepared by microwave sintering

Synergistic effects of TiC and graphene on the microstructure and tribological properties of Al2024 matrix composites