Abstract:The back interface of the flexible solar cell is effectively tailored through electrochemical polishing and UV‐O3 treatment, resulting in high‐quality CZTSSe film and a quasi‐ohmic contact, leading to a significant improvement in efficiency, and highlighting the critical importance of back contact interfaces for efficient carrier collection in flexible thin film solar cells. Flexible Cu2ZnSn(S,Se)4 (CZTSSe) solar cells is attracting much attention because of their enormous application prospects. However, current flexible CZTSSe solar cells with Mo foil as substrate still suffer from severe back interface problems due to the complexity of substrate surfaces. Herein, a facile approach to tailor the surface of the flexible substrate and modify the back interface between CZTSSe and Mo foil is proposed. The study discloses that a simple polishing can not only improve the wettability of the precursor solution on the substrate unexpectedly and thus improve the quality of the CZTSSe film, but also increase the mechanical stability of the absorber layer grown on Mo foil. The subsequent UV‐ozone treatment helps to form a favorite MoO3 layer for efficient CZTSSe devices. Surprisingly, the quasi‐ohmic contact is formed between CZTSSe/Mo foil by such combined treatments and thus promoting the carrier collection. Consequently, the efficiency of the flexible CZTSSe solar cell is significantly improved from 4.94% to 10.32% without anti‐reflection layer. The bending durability of the cell fabricated on the treated Mo foil is increased greatly. This work discloses that back contact interface is very important for the carrier collection and thus the highly efficient flexible thin film solar cells.

Efficiency Improvement of Flexible Cu2ZnSn(S,Se)4 Solar Cells by Window Layer Interface Engineering

Optimizing the window layer for achieving over 10% efficient Cu2ZnSn(S,Se)4 solar cells

10.24% Efficiency of Flexible Cu2 ZnSn(S,Se)4 Solar Cells by Pre-Evaporation Selenization Technique

Toward High Efficient Cu2 ZnSn(Sx ,Se1- x )4 Solar Cells: Break the Limitations of VOC and FF

Heterojunction interface regulation to realize high-performance flexible Kesterite solar cells

Antimony incorporated flexible Cu 2 ZnSn(S,Se) 4 solar cell for enhanced mechanical endurance and efficiency

Role of zinc tin oxide passivation layer at back electrode interface in improving efficiency of Cu2ZnSn(S,Se)4 solar cells

High-efficiency CdTe-based Thin-Film Solar Cells with Unltrathin CdS:O Window Layer and Processes with Post Annealing

CdS(In)/CZTSSe bandgap alignment engineering for performance enhancement of solar cells without ZnO layer

Facile Tailor on the Surface of Mo Foil Toward High‐Efficient Flexible CZTSSe Solar Cells

N‐Type Surface Design for p‐Type CZTSSe Thin Film to Attain High Efficiency

High-efficient Sb 2 Se 3 solar cell using Zn x Cd 1- x S n-type layer

In-doping collaboratively controlling back interface and bulk defects to achieve efficient flexible CZTSSe solar cells

Surprising Efficiency Enhancement of Cu 2 ZnSn(S,Se) 4 Solar Cells with Abnormal Zn/Sn Ratios

Realization of 11.5% Efficiency Cu 2 ZnSn(S,Se) 4 Thin‐Film Solar Cells by Manipulating the Phase Structure of Precursor Films

An ITO‐Free Kesterite Solar Cell

Improving the Performance of Cu2ZnSn(S,Se)4 Thin Film Solar Cells by SCAPS Simulation

The enhancement of CZTSSe solar cell performance through active construction of the double-layer absorber

Cu2ZnSn(S, Se)4 solar cell with slight band tailing states achieves 11.83% efficiency by selenizing sputtered Cu–Zn–Sn–S precursor

Flexible Monolithic 2-Terminal Kesterite Cu2ZnSnSe4 /perovskite Tandem Solar Cells

Interface optimization and defects suppression via NaF introduction enable efficient flexible Sb 2 Se 3 thin-film solar cells