Abstract:In this paper, excellent performance W-Cu-Ni-Fe alloys with the addition of Ni and Fe (total content: 5 wt%) were successfully prepared by low temperature liquid-phase sintering, using the raw material of ultrafine W-Cu-Ni-Fe composite powder. Ultrafine W-Cu-Ni-Fe composite powder with high sintering activity and uniform composition distribution was prepared by a two-stage reduction method consisting of carbothermal reaction and hydrogen deep deoxidation. Additions of Ni and Fe not only improved the wettability between W and Cu two phases, but also improved the bonding strength of two-phase interface. All sintered samples had higher relatively densities to ensure that the samples have great comprehensive properties. When Ni and Fe were co-added in appropriate proportions, the highest tensile strength and elongation of W-Cu-Ni-Fe alloy samples were 497 MPa and 9.12 % for the composition: W-3.5 wt%Ni-1.5 wt%Fe-25 wt%Cu, respectively. Meanwhile, with increasing Ni content from 0 wt% to 5 wt%, the compressive strength and failure strain of alloy samples increased from 1160 MPa to 2376 MPa and from 53 % to 98 %, respectively. In addition, with the enhancement of the solid solution strengthening effects of Ni and Fe on Cu matrix, the bending strength and microhardness of the alloy samples increased to 1174 MPa and 361 HV for composition: W-3.5 wt%Ni-1.5 wt%Fe-25 wt%Cu, respectively. Although the additions of Ni and Fe made the Cu matrix network structure have a uniform distribution, it led to a decrease in the electron transfer ability of the alloy, and thus, there was a decrease in electrical conductivity.

Influence of Ni additions on the microstructure and tensile property of W-Cu composites produced by direct energy deposition

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Preparation and properties of W-30 wt% Cu alloy with the additions of Ni and Fe elements

Effect of Ni Content on Microstructure and Properties of WC-Ni Composites Prepared by Electroless Plating and Powder Metallurgy

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Effect of Microalloying Addition on Microstructure and Mechanical Properties of Ni-W Coatings

Microstructure and Tensile Properties of Ni Nano Particles Modified MXene Reinforced Copper Matrix Composites

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Effect of Ni Additive on the Microstructure of TiB2-Cu Matrix Composites

Influence of Ni-P content on microstructure and mechanical properties of Fe-x(Ni+P)-1Cu alloys

Mechanical properties and superplasticity of the Ni/Si3N4(W) nanocomposite fabricated by electrodeposition

Effect of nano-Y2O3 on the microstructure and mechanical properties of Cu-10W composites prepared by spark plasma sintering

Insight into the Microstructure and Tensile Behavior of the W–Cu Composite Reinforced with Tungsten Fibers and Particulates

Fabrication and characterization of W/Cu/Ni-based high specific gravity alloy with Zr and Ti combined addition

Influence of Ni-CNTs additions on the microstructure and mechanical properties of extruded Mg-9Al alloy

Effects of Ni and Cu Additions on Microstructures, Mechanical Properties and Wear Resistances of Ultra-Coarse Grained WC–6Co Cemented Carbides

Enhanced interfacial wettability and mechanical properties of Ni@Al2O3/Cu ceramic matrix composites using spark plasma sintering of Ni coated Al2O3 powders

Microstructural studies of W–10wt.% Cu composites prepared by using ultrafine composite powder

Enhanced mechanical properties and thermal conductivity of W-30Cu composite fabricated with monodisperse and nearly spherical W powder

Influences of Carbon Nanotubes on Performance of W-Cu Composite Materials