Abstract:In order to solve problems of significant interfacial reactions and agglomeration in graphene reinforced W-Cu composites, powders of copper coated graphene (Cu@Gr) were pre-mechanically mixed with tungsten and copper powders, and then graphene doped W-Cu composites were sintered using two different methods, e.g., spark plasma sintering (SPS) and infiltration sintering. Microstructural analysis showed that the doped Cu@Gr powder can effectively inhibit the interfacial reaction between graphene and tungsten, prevent the segregation of graphene, and evenly distribute the copper in the binder phase. When the mixed concentration of Cu@Gr was 0.45 wt%, uniform distributions of W phase and Cu phase were obtained in the composite, and the mechanical properties and conductivity of this composite achieved their best results. When the doping content was further increased to 0.8%, WC phase was found in all alloys, thus resulting in poor mechanical and physical properties. Comparing the microstructures produced using these two methods, the composites prepared using the infiltration sintering method showed network distribution of copper phase and segregation of copper, whereas the composites prepared using the SPS method showed network skeleton phase of tungsten. Although the SPS process was performed in a much shorter time, the mechanical properties of the composites sintered using the SPS process did not show much differences with those sintered using the infiltration sintering method.

Effect of nano-Y2O3 on the microstructure and mechanical properties of Cu-10W composites prepared by spark plasma sintering

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Multiphase strengthening mechanism of Cu-Y2O3/W composites prepared by mechanical alloying

Microstructure and properties of Y2O3/Cu composites fabricated by a novel liquid phase in situ reactive synthesis process

Effects of solid–liquid doping and spark plasma sintering on the microstructure and mechanical properties of Y2O3-doped copper matrix composites

Effect of alloying element Zr on microstructure and properties of Cu−Y2O3 composites

Effect of sintering temperature on fine-grained Cu W composites with high copper

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

The Effect of Y2O3 Particles on the Microstructure and Mechanical Properties of Tungsten Fiber-Reinforced Tungsten Composites

Effects of composite oxide addition on the microstructure and properties of ODS copper

Effect of spark plasma sintering temperature on structure and performance characteristics of Cu-20wt%W composite

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures

Microstructure and electrical contact behavior of Al2O3–Cu/30W3SiC(0.5Y2O3) composites

Excellent performance of W–Y2O3 composite via powder process improvement and Y2O3 refinement

Development of Y2O3 Dispersion-Strengthened Copper Alloy by Sol-Gel Method

The effects of ultrasonic vibration on mechanical properties of tungsten particle-reinforced copper-matrix composites

Enhanced mechanical properties and thermal conductivity of W-30Cu composite fabricated with monodisperse and nearly spherical W powder

Effect of Silver Element on Microstructure and Properties of W-30Cu/TiC Composites

W-Cu Composites Reinforced by Copper Coated Graphene Prepared Using Infiltration Sintering and Spark Plasma Sintering: A Comparative Study

Fabrication and microstructure of W-Cu composites prepared from Ag-coated Cu powders by electroless plating