Effect of Ni Additive on the Microstructure of TiB2-Cu Matrix Composites

徐强,张幸红,韩杰才,赫晓东

DOI: https://doi.org/10.3969/j.issn.1001-4381.2003.11.004

2003-01-01

Journal of Materials Engineering

Abstract:TiB_2-Cu matrix composites were in-situ produced via combustion synthesis.Nickel, as an alloy element, was added into TiB_2-Cu composite to improve the wettability between titanium diboride and copper matrix.The effect of nickel additive on the microstructures of TiB_2-Cu matrix composites was investigated using XRD, SEM, EPMA and TEM.The results show that the face spaces of metal binder in TiB_2-Cu-Ni composite are lower than those in TiB_2-Cu composite.With the addition of nickel, the microstructure of TiB_2-Cu-Ni composite is denser than that of TiB_2-Cu composite, while the size of TiB_2 particles is larger than that in TiB_2-Cu composite.Some TiB_2 particles have enough time to grow in block-like shape because the thermal conductivity and cooling rate of composite reduce with the addition of nickel.Moreover, more sintering-necking between TiB_2 particles and particles are formed in TiB_2-Cu-Ni composite.The interfacial bonding between TiB_2 and metal binder is good and no interfacial debonding or interface crack is found in TiB_2-Cu-Ni composite due to improvement of wettability between TiB_2 and metal binder.The research has led to the discovery of improvement of microstructure and densification of TiB_2-Cu matrix composites due to the addition of nickel.