Abstract:In order to investigate the effect of TiB2 contents on the microstructure and wear resistance of titanium matrix composites, commercial pure Ti (CP-Ti) powders with 0–7.5 wt.% TiB2 particles were melted by selective laser melting (SLM) to produce the in-situ Ti-TiB composites. When the TiB2 content increases from 2.5 wt.% to 7.5 wt.%, the microstructures of the Ti-TiB composites undergo a transition from the single phase of α′-Ti to the mixed phases of α′-Ti, TiB and TiB2, and the acicular α′-Ti is refined significantly from 1.03 ± 0.24 μm to 0.36 ± 0.05 μm, showing that increasing the TiB2 content induces the formation of TiB and refines the microstructure. Moreover, large TiB2 particles are not melted completely and they react with the Ti matrix liquid to form a TiB layer around the Ti matrix during SLM. However, small TiB2 particles are completely dissolved into the Ti matrix liquid so that the eutectic TiB grains are precipitated at the boundaries of the Ti matrix after in-situ reaction of TiB2 with Ti. The formation of α′ martensite in the titanium matrix and the addition of TiB2 can induce the fine grain strengthening, the dispersion strengthening, the solid solution strengthening in the SLM-produced composites. The results indicate that the microhardness of the composites increases from 258 ± 10.3 HV0.2 to 435 ± 14.7 HV0.2. The wear process of the SLM-produced CP-Ti and TiB2 reinforced Ti matrix composites is accompanied by adhesion wear, abrasive wear and oxidation wear. As a result, when the TiB2 content increases to 7.5%, the wear resistance of the composites increases by 32.6% compared with that of the CP-Ti. These improvements are mainly due to strengthening and hardening effects induced by TiB2 particles and refinement of Ti matrix. This study provides some basis for developing wear-resistant and high-strength titanium alloys.

Effect of TiB2 content on microstructure and properties of in situ Ti-TiB composites

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

IN SITU TiBW/Ti COMPOSITES WITH A NOVEL QUASI- CONTINUOUS NETWORK REINFORCEMENT ARCHITECTURE

High Temperature Tensile Properties of in Situ TiBw/Ti6Al4V Composites with a Novel Network Reinforcement Architecture

Microstructure and Wear-resistant Properties of in situ TiB-TiC Reinforced Titanium Matrix Composites by Laser Deposition Manufacturing

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

Microstructure and mechanical properties of (TiB+TiC)/Ti composites fabricated in situ via selective laser melting of Ti and B4C powders

The Effect of Micron-Sized TiB2 Particles on the Properties of Al6061 Strengthened with 4% TiB2 Nano-TiB2

Microstructure and mechanical properties of in-situ hybrid reinforced (TiB+TiC)/Ti composites prepared by laser powder bed fusion

Microstructural characterization and mechanical properties of (TiC+TiB)/TA15 composites prepared by an in-situ synthesis method

TiB Whisker and Nitrogen Solid‐Solution Synergistic‐Strengthened Titanium Matrix Composites by Ti–BN via Spark Plasma Sintering and Hot Extrusion

Microstructure and Mechanical Properties of Cu Matrix Composites Reinforced by TiB2/TiN Ceramic Reinforcements

Microstructure of In-Situ Synthesized (tib+tic)/ti Composites Prepared by Hot-pressing

Microstructure and strengthening mechanism of boride in-situ reinforced titanium matrix composites prepared by plasma activated sintering

Effects of TiB Volume Fraction on the Microstructure and Mechanical Properties of TiBw/TA15 Composites with Novel Columnar Structure

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Investigation on mechanical and tribological behaviour of titanium diboride reinforced martensitic stainless steel

Refined microstructure and enhanced wear resistance of titanium matrix composites produced by selective laser melting

Effects of TiB2 Particles on the Microstructure Evolution and Mechanical Properties of B4C/TiB2 Ceramic Composite

In-Situ Synthesis, Microstructure, and Mechanical Properties of TiB2-Reinforced Fe-Cr-Mn-Al Steel Matrix Composites Prepared by Spark Plasma Sintering

Microstructure and Mechanical Properties of In Situ TiB2/2024 Composites Fabricated by Powder Metallurgy