Microstructure mechanical properties and tribological properties of high entropy M 2 AlC-MC (M = Ti, V, Zr, Hf, Ta) composites prepared via spark plasma sintering
Haoran Zou,Jinyong Zhang,Lin Ren,Weimin Wang,Fan Zhang,Zhengyi Fu
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.10.018
IF: 5.7
2023-11-21
Journal of the European Ceramic Society
Abstract:M 2 AlC-MC (M = Ti, V, Zr, Hf, Ta) HECs were successfully synthesized via SPS. The microstructure were characterized by XRD, SEM, TEM , EDS, and Maud software was used for Rietveld refinement analysis of phase composition content. The results showed that Ti, V, Zr, Hf, and Ta elements were successfully dissolved in both M 2 AlC and MC. On this basis, the density, hardness and mechanical properties were tested. The results showed that hardness and mechanical properties of M 2 AlC-MC HECs were better than those of traditional M 2 AlC and their composites except for a slight decrease in fracture toughness. For the first time, the tribological properties of M 2 AlC-MC HECs were studied, and the measured friction coefficient was less than 0.66, and the wear rate was 1.76 × 10 −4 mm 3 N −1 m −1 . This work can provide important reference for the subsequent preparation of M 2 AlC-MC HECs and further expand the development field of friction resistant materials.
materials science, ceramics