Abstract:During the fabrication of an indium-gallium-zinc oxide (IGZO) thin film transistor (TFT), the thermal process was used to reduce the resistivity of IGZO. The annealing temperature was found to have great influence on the transistor characteristics. At an optimized heat-treatment temperature, the depletion-mode IGZO TFT was fabricated with steeper subthreshold slope, higher filed-effect mobility and acceptable turn-on voltage. And the relatively conductive IGZO could directly replace the indium tin oxide as the transparent electrode of the organic light-emitting diode (OLED), reducing the mask count of the backplane for the active-matrix OLED display. INTRODUCTION Thin film transistor (TFT) based on metal oxide (MO), especially, indium-gallium-zinc oxide (IGZO), is considered as a good candidate to fabricate large area backplane for active-matrix organic light-emitting diode (AMOLED) display, due to its high mobility, good uniformity and low off-state current [1]. Our previous study [2] suggested that the resistivity (ρ) of IGZO highly depended on the heat-treatment conditions, such as annealing ambience, temperature, duration and gas permeability of IGZO cover, while the thermal process was often inevitable during the fabrication of IGZO TFT. With the active layer of IGZO covered with the gas-permeable silicon oxide (SiOx), the TFT was subjected to a serious anneals in an oxygen-deficient nitrogen (N2) ambience. With the increasing temperature, although the mobility was enhanced, the turn-on voltage (Von) became more and more negative. At an optimized temperature, the depletion-mode (DM) IGZO TFT with steeper subthreshold slope, higher filed-effect mobility and acceptable turn-on voltage was fabricated. Furthermore, such annealing-induced conductive IGZO source/drain regions can be directly used to replace the indium tin oxide (ITO) as the transparent electrode of OLED, reducing the mask count of AMOLED backplane. Annealing-Induced DM IGZO TFT Shown in Figure 1 is the evolution of the schematic cross-section of an IGZO TFT. A gate dielectric of 100 nm silicon oxide (SiOx) was first thermally grown on an n+ silicon substrate, which served as the gate electrode. 10 or 20 nm IGZO film was then room-temperature sputtered using a target of In2O3:Ga2O3:ZnO = 1:1:1 mol% in an atmosphere of 10% oxygen (O2) and 90% argon (Ar). After the patterning of the active-island using the hydrofluoric acid, a passivation layer of 300 nm SiOx was deposited at 300 oC in a plasma-enhanced chemical vapor deposition (PECVD) reactor. The tetraethylorthosilicate (TEOS) and O2 were used as the source gases. The contact holes were then opened and the resulting structure was subjected to a series of anneals, as shown in Figure 1a. Finally, 300 nm aluminum (Al) was deposited and patterned into electrodes (Fig. 1b). These TFTs were measured using an Agilent 4156C semiconductor parameter analyzer. n+ Si 100nm SiOx 300nm SiOx

P-22: Turn-On Voltage Modulation of Indium-Gallium-Zinc-Oxide Thin-Film Transistors Through Thermal Annealing Processes

Highly Stable Atomic Layer Deposited Zinc Oxide Thin-Film Transistors Incorporating Triple O 2 Annealing

Thermally Induced Variation of the Turn-ON Voltage of an Indium–Gallium–Zinc Oxide Thin-Film Transistor

Influence of Post-Annealing on Electrical Characteristics of Thin-Film Transistors with Atomic-Layer-Deposited Zno-Channel/Al2o3-Dielectric

Effects of Annealing Process on Characteristics of Fully Transparent Zinc Tin Oxide Thin-Film Transistor

Performance Improvement of Atomic Layer-Deposited ZnO/Al2O3Thin-Film Transistors by Low-Temperature Annealing in Air

Tuning the electrical properties of ZnO thin-film transistors by thermal annealing in different gases

P‐18: Student Poster: Non‐Oxidizing Pre‐Annealing for Enhanced Fluorination of an Indium‐Gallium‐Zinc Oxide Thin‐Film Transistor

P‐1.2: Photoluminescence and Electrical Properties Study of ITO‐stabilized ZnO Thin‐Film Transistors with Different Annealing Temperatures

Annealing-Induced Depletion-Mode Indium-Gallium-Zinc Oxide Thin-Film Transistor and Its Application to Active-Matrix Organic Light-Emitting Diode Display

Mobility Enhancement and OFF Current Suppression in Atomic-Layer-Deposited ZnO Thin-Film Transistors by Post Annealing in O2

The Influence of Annealing Temperature on Amorphous Indium‐Zinc‐Tungsten Oxide Thin‐Film Transistors

Solution-processed IGZO field-effect transistors with a three-step laser annealing process

Solution-processed indium gallium zinc oxide thin-film transistors with infrared irradiation annealing

Enhancement of Two-Step Low-Temperature Annealing Treatment on Electrical Performance of In-Sn-O Thin-Film Transistors

Characteristics of Elevated-Metal Metal-Oxide Thin-Film Transistors Based on Indium-Tin-Zinc Oxide

Annealing Effect on Amorphous Indium-Zinc-Tungsten-Oxide Thin-Film Transistors

Stability Study of Indium Tungsten Oxide Thin-Film Transistors Annealed under Various Ambient Conditions

An Oxidation-Last Annealing for Enhancing the Reliability of Indium-Gallium-zinc Oxide Thin-Film Transistors

High Performance RF Sputtering Deposited AZO Thin-Film Transistors after a Post-Annealing Process

Improvement of Device Characteristics of Low Temperature IGZO Thin-film Transistors through Laser Post Annealing