Abstract:During the fabrication of an indium-gallium-zinc oxide (IGZO) thin film transistor (TFT), the thermal process was used to reduce the resistivity of IGZO. The annealing temperature was found to have great influence on the transistor characteristics. At an optimized heat-treatment temperature, the depletion-mode IGZO TFT was fabricated with steeper subthreshold slope, higher filed-effect mobility and acceptable turn-on voltage. And the relatively conductive IGZO could directly replace the indium tin oxide as the transparent electrode of the organic light-emitting diode (OLED), reducing the mask count of the backplane for the active-matrix OLED display. INTRODUCTION Thin film transistor (TFT) based on metal oxide (MO), especially, indium-gallium-zinc oxide (IGZO), is considered as a good candidate to fabricate large area backplane for active-matrix organic light-emitting diode (AMOLED) display, due to its high mobility, good uniformity and low off-state current [1]. Our previous study [2] suggested that the resistivity (ρ) of IGZO highly depended on the heat-treatment conditions, such as annealing ambience, temperature, duration and gas permeability of IGZO cover, while the thermal process was often inevitable during the fabrication of IGZO TFT. With the active layer of IGZO covered with the gas-permeable silicon oxide (SiOx), the TFT was subjected to a serious anneals in an oxygen-deficient nitrogen (N2) ambience. With the increasing temperature, although the mobility was enhanced, the turn-on voltage (Von) became more and more negative. At an optimized temperature, the depletion-mode (DM) IGZO TFT with steeper subthreshold slope, higher filed-effect mobility and acceptable turn-on voltage was fabricated. Furthermore, such annealing-induced conductive IGZO source/drain regions can be directly used to replace the indium tin oxide (ITO) as the transparent electrode of OLED, reducing the mask count of AMOLED backplane. Annealing-Induced DM IGZO TFT Shown in Figure 1 is the evolution of the schematic cross-section of an IGZO TFT. A gate dielectric of 100 nm silicon oxide (SiOx) was first thermally grown on an n+ silicon substrate, which served as the gate electrode. 10 or 20 nm IGZO film was then room-temperature sputtered using a target of In2O3:Ga2O3:ZnO = 1:1:1 mol% in an atmosphere of 10% oxygen (O2) and 90% argon (Ar). After the patterning of the active-island using the hydrofluoric acid, a passivation layer of 300 nm SiOx was deposited at 300 oC in a plasma-enhanced chemical vapor deposition (PECVD) reactor. The tetraethylorthosilicate (TEOS) and O2 were used as the source gases. The contact holes were then opened and the resulting structure was subjected to a series of anneals, as shown in Figure 1a. Finally, 300 nm aluminum (Al) was deposited and patterned into electrodes (Fig. 1b). These TFTs were measured using an Agilent 4156C semiconductor parameter analyzer. n+ Si 100nm SiOx 300nm SiOx

Solution-processed indium gallium zinc oxide thin-film transistors with infrared irradiation annealing

Influence of Annealing Temperatures on Solution-Processed Alinzno Thin Film Transistors

Solution-processed IGZO field-effect transistors with a three-step laser annealing process

Transparent Amorphous Indium-Gallium-Zinc-Oxygen Thin Film Transistors Using Solution Technology at Low Temperature

Characteristic Enhancement of Solution-Processed In–Ga–Zn Oxide Thin-Film Transistors by Laser Annealing

Annealing-Induced Depletion-Mode Indium-Gallium-Zinc Oxide Thin-Film Transistor and Its Application to Active-Matrix Organic Light-Emitting Diode Display

Impact of pre-annealing process on electrical properties and stability of indium zinc oxide thin-film transistors

Low-Temperature Rapid Preparation of High-Performance Indium Oxide Thin Films and Transistors Based on Solution Process

Rapid thermal annealing effect on performance variations of solution processed indium–gallium–zinc-oxide thin-film transistors

High-Performance a-IGZO TFT Fabricated With Ultralow Thermal Budget via Microwave Annealing

High-Performance Solution-Processed Amorphous InGaZnO Thin Film Transistors with a Metal–Organic Decomposition Method

Fabrication and performance of indium oxide based transparent thin film transistors

Rapid preparation of solution-processed InGaZnO thin films by microwave annealing and photoirradiation

Improvement of device characteristics of plasma-treated indium gallium zinc oxide thin-film transistors through thermal annealing

Intense pulsed light annealing of solution-based indium-gallium-zinc-oxide semiconductors with printed Ag source and drain electrodes for bottom gate thin film transistors

Annealing Effect on Amorphous Indium-Zinc-Tungsten-Oxide Thin-Film Transistors

Sol–gel processed indium zinc oxide thin film and transparent thin-film transistors

Mechanochemical and Thermal Treatment for Surface Functionalization to Reduce the Activation Temperature of In-Ga-Zn-O Thin-film Transistors

Low-Temperature Fabrication of IZO Thin Film for Flexible Transistors

The improved properties of solution-based InGaSnO (IGTO) thin film transistor using the modification of InZnO (IZO) layer

Fabrication of Transparent Indium Zinc Oxide Thin Film Transistors by Sol-gel Technology