Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling
Xuezhang Xiao,Xinhua Wang,Linhui Gao,Li Wang,Changpin Chen
DOI: https://doi.org/10.1016/j.jallcom.2005.06.064
IF: 6.2
2006-01-01
Journal of Alloys and Compounds
Abstract:Amorphous 2Mg–Fe+xwt.% Ni alloys were synthesized by mechanical alloying of Mg and Fe elemental powders. Two kinds of ball-milling atmospheres, namely, (1) under argon and (2) first under argon and then in tetrahydrofuran (THF), were examined in this study. The effects of the Ni addition and ball-milling time and atmosphere on the microstructure and electrochemical properties of the prepared alloys have been investigated systematically. The results show that the ball-milled (2Mg–Fe) nickel-free mixture still maintains Mg and Fe elemental phases, and its discharge capacity is only 19.2mAhg−1. The Ni powder addition is advantageous for the formation of Mg–Fe amorphous structure and for the improvement of the electrochemical properties of the alloys. For the alloys milled under argon, with the Ni content x increasing, the discharge capacity of the alloys increases first and then decreases, and reaches a maximum value of 455.3mAhg−1 as x=100. With the milling-time extending, the discharge capacity of the alloy increases first and then decreases too. For the alloys milled under argon and then in THF, the alloys exhibit higher degree of amorphorization, bigger specific surface area and more active surfaces, and thus have better electrochemical properties than those milled under argon. With the Ni increasing, the discharge capacity increases from 249.7mAhg−1 (x=50) to 565.2mAhg−1 (x=150) and then decreases to 497.9mAhg−1 (x=200), and the exchange current density I0 increases from 104.8mAg−1 (x=50) to 251.1mAg−1 (x=200), which is consistent with the variation of the HRD of the alloy electrodes in the investigation range.