Abstract:Co-free MlNi(4.1)Mn(0.35)Al(0.3)Fe(0.25) (Ml: La-rich mischmetal) alloy samples were prepared in three different ways. The original as-cast alloy was prepared by vacuum levitation melting in a cold crucible. One-third of the as-cast ingot was annealed at 1273 K for 10 h, and another one-third was remelted and rapidly solidified by melt-spinning. The influence of the alloy preparation methods on their microstructure and electrochemical properties was studied. XRD and SEM results revealed that all of the three differently prepared alloys were of the single CaCu5-type structure phase, but their microstructure and electrochemical properties were changed markedly. The as-cast alloy had a typical dendrite structure with noticeable composition segregation and rather poor cycling endurance. While the annealed and melt-spun alloy were of an equiaxed structure and a very fine cellular structure, respectively, and had a more homogeneous composition and dramatically improved cycling endurance, although their activation rate and high-rate dischargeability were lowered somewhat. In this study, the melt-spun Co-free alloy showed the best cycling stability (S-500 = 69.2%) and a reasonably high capacity (305 mA h g(-1)) and 1C rate dischargeability (85.6%), which is attributed to its lower degree of pulverization and more uniform composition. (C) 2002 Elsevier Science B.V. All rights reserved.

Enhanced Electrochemical Properties of Ball-Milled Ti-30v-15mn-15cr+20 Wt% La(Nimncoal)(5) Alloy Electrodes

Effects of Surface Modification on the Electrode Behavior of Ball-Milled La2Mg17 + 200 Wt% Ni Composite in Alkaline Solution

Electrochemical Performance of Ti[sub 0.4]v[sub 0.3]mn[sub 0.15]cr[sub 0.15] Alloy Surface-Modified by Ballmilling with LaNi[sub 3.55]co[sub 0.75]mn[sub 0.4]al[sub 0.3]

Electrochemical performance of ball-milled Ti–V-based electrode alloy

Electrochemical Performance of the Ball-Milled La2Mg14−xTixNi3 Alloys with Ni Powders (x=1 and 2)

Electrochemical Properties of Cemg12+X%Ni Composites (X=0 Similar to 200) Prepared by Ball-Milling

Effect of ball-milling time on the electrochemical performance of ball-milled LaMg11Ni+200wt% Ni composite

Influence of the material processing on the electrochemical properties of cobalt-free Ml(NiMnAlFe)5 alloy

Enhanced Electrochemical Performance of LiNi0.8Co0.15Al0.05O2 Cathode Material via Li2TiO3 Nanoparticles Coating

Preparations and Electrochemical Properties of Amorphous Ti-Al Alloys

Microstructure and electrochemical properties of amorphous composites of ball-milled Mg2Ni0.95Sn0.05 + x wt% Ni

Effects of ball-milling time and Bi2O3 addition on electrochemical performance of ball-milled La2Mg17+200wt.% Ni composites

Influence of Annealing Treatment on Microstructure and Cycling Stability of La-Rich Ml(Nicomnal)(5) Alloy Electrode for Ni/Mh Batteries

The Electrochemical Evaluation of Ball Milled MgNi-based Hydrogen Storage Alloys

Electrode properties of La2Mg17 alloy ball-milled with x wt.% cobalt powder (x = 50, 100, 150 and 200)

Microstructure and Electrochemical Properties of Mechanically Ground Ce2Mg17 + X Wt.% Ni (x = 0, 50, 100, 200) Composites

Electrochemical Properties of Cemg11ni+X% Ni Composites (X=0, 50, 100 and 200) Prepared by Ball-Milling

Effect of Ni content on the electrochemical performance of the ball-milled La2Mg17-xNix + 200 wt.% Ni (x = 0, 1, 3, 5) composites

The Structure and Electrochemical Properties of Ball-Milled Ti0.9Zr0.2Mn1.6Ni0.2V0.2 Alloys

Electrode Characteristics of Non-Stoichiometric Ml(Nimnalfe)(X) Alloys

Influence of Ball-Milling with Cu Powder on Electrochemical Properties of V-based Solid Solution Type Hydrogen Storage Alloys