Abstract:Amorphous 2Mg–Fe+xwt.% Ni alloys were synthesized by mechanical alloying of Mg and Fe elemental powders. Two kinds of ball-milling atmospheres, namely, (1) under argon and (2) first under argon and then in tetrahydrofuran (THF), were examined in this study. The effects of the Ni addition and ball-milling time and atmosphere on the microstructure and electrochemical properties of the prepared alloys have been investigated systematically. The results show that the ball-milled (2Mg–Fe) nickel-free mixture still maintains Mg and Fe elemental phases, and its discharge capacity is only 19.2mAhg−1. The Ni powder addition is advantageous for the formation of Mg–Fe amorphous structure and for the improvement of the electrochemical properties of the alloys. For the alloys milled under argon, with the Ni content x increasing, the discharge capacity of the alloys increases first and then decreases, and reaches a maximum value of 455.3mAhg−1 as x=100. With the milling-time extending, the discharge capacity of the alloy increases first and then decreases too. For the alloys milled under argon and then in THF, the alloys exhibit higher degree of amorphorization, bigger specific surface area and more active surfaces, and thus have better electrochemical properties than those milled under argon. With the Ni increasing, the discharge capacity increases from 249.7mAhg−1 (x=50) to 565.2mAhg−1 (x=150) and then decreases to 497.9mAhg−1 (x=200), and the exchange current density I0 increases from 104.8mAg−1 (x=50) to 251.1mAg−1 (x=200), which is consistent with the variation of the HRD of the alloy electrodes in the investigation range.

Electrochemical Properties of Cemg11ni+X% Ni Composites (X=0, 50, 100 and 200) Prepared by Ball-Milling

Electrochemical Properties of Cemg12+X%Ni Composites (X=0 Similar to 200) Prepared by Ball-Milling

Electrochemical Properties of CeMg12＋x% Ni Composites （x=0～200） Prepared by Ball-Milling

Microstructure and Electrochemical Properties of Mechanically Ground Ce2Mg17 + X Wt.% Ni (x = 0, 50, 100, 200) Composites

Microstructure and electrochemical properties of amorphous composites of ball-milled Mg2Ni0.95Sn0.05 + x wt% Ni

Effects of Surface Modification on the Electrode Behavior of Amorphous CeMg12 Alloys

Mechanical Ball Milling Preparation and Electrochemical Hydrogen Storage Properties of Amorphous Mg-Fe Composites

Influence of Ball-milling with Ni Powder on the Phase Structure and Electrochemical Hydrogen Storage Properties of Mg17Al12 Alloy

Effects of Surface Coating on the Electrochemical Properties of Amorphous CeMg12 Composite

Microstructure and Properties of In-Situ TiC Reinforced Copper Nanocomposites Fabricated Via Long-Term Ball Milling and Hot Pressing

Electrochemical Performance of the Ball-Milled La2Mg14−xTixNi3 Alloys with Ni Powders (x=1 and 2)

Effect of ball-milling time on the electrochemical performance of ball-milled LaMg11Ni+200wt% Ni composite

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

Effects of Surface Modification on the Electrode Behavior of Ball-Milled La2Mg17 + 200 Wt% Ni Composite in Alkaline Solution

Microstructure and electrochemical properties of amorphous Mg-Fe-Ni hydrogen storage electrode material

Microstructures and electrochemical hydrogen storage properties of novel Mg–Al–Ni amorphous composites

Effect of Ni content on the electrochemical performance of the ball-milled La2Mg17-xNix + 200 wt.% Ni (x = 0, 1, 3, 5) composites

Electrochemical Hydrogen Discharge Properties of MgNi-Carbon Nanotube Composites

Effects of ball-milling time and Bi2O3 addition on electrochemical performance of ball-milled La2Mg17+200wt.% Ni composites

The Electrochemical Evaluation of Ball Milled MgNi-based Hydrogen Storage Alloys

Influence of Ball-Milling with Cu Powder on Electrochemical Properties of V-based Solid Solution Type Hydrogen Storage Alloys