Abstract:Amorphous 2Mg–Fe+xwt.% Ni alloys were synthesized by mechanical alloying of Mg and Fe elemental powders. Two kinds of ball-milling atmospheres, namely, (1) under argon and (2) first under argon and then in tetrahydrofuran (THF), were examined in this study. The effects of the Ni addition and ball-milling time and atmosphere on the microstructure and electrochemical properties of the prepared alloys have been investigated systematically. The results show that the ball-milled (2Mg–Fe) nickel-free mixture still maintains Mg and Fe elemental phases, and its discharge capacity is only 19.2mAhg−1. The Ni powder addition is advantageous for the formation of Mg–Fe amorphous structure and for the improvement of the electrochemical properties of the alloys. For the alloys milled under argon, with the Ni content x increasing, the discharge capacity of the alloys increases first and then decreases, and reaches a maximum value of 455.3mAhg−1 as x=100. With the milling-time extending, the discharge capacity of the alloy increases first and then decreases too. For the alloys milled under argon and then in THF, the alloys exhibit higher degree of amorphorization, bigger specific surface area and more active surfaces, and thus have better electrochemical properties than those milled under argon. With the Ni increasing, the discharge capacity increases from 249.7mAhg−1 (x=50) to 565.2mAhg−1 (x=150) and then decreases to 497.9mAhg−1 (x=200), and the exchange current density I0 increases from 104.8mAg−1 (x=50) to 251.1mAg−1 (x=200), which is consistent with the variation of the HRD of the alloy electrodes in the investigation range.

Electrochemical Performance of the Ball-Milled La2Mg14−xTixNi3 Alloys with Ni Powders (x=1 and 2)

Effect of Ni content on the electrochemical performance of the ball-milled La2Mg17-xNix + 200 wt.% Ni (x = 0, 1, 3, 5) composites

Microstructure and electrochemical properties of amorphous composites of ball-milled Mg2Ni0.95Sn0.05 + x wt% Ni

Effects of Surface Modification on the Electrode Behavior of Ball-Milled La2Mg17 + 200 Wt% Ni Composite in Alkaline Solution

Influence of Ball-milling with Ni Powder on the Phase Structure and Electrochemical Hydrogen Storage Properties of Mg17Al12 Alloy

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

Influence of Ball-Milling with Cu Powder on Electrochemical Properties of V-based Solid Solution Type Hydrogen Storage Alloys

Preparations and Electrochemical Properties of Amorphous Ti-Al Alloys

PHASE STRUCTURE AND ELECTROCHEMICAL PROPERTIES OF La-Mg-Ni SYSTEM AB_3 TYPE HYDROGEN STORAGE ELECTRODE ALLOYS

Microstructures and electrochemical hydrogen storage properties of novel Mg–Al–Ni amorphous composites

The structural and electrochemical properties of La2Mg(Ni0.8-xCo0.2Alx)9 (x = 0-0.03) hydrogen storage electrode alloys

Effect of ball-milling time on the electrochemical performance of ball-milled LaMg11Ni+200wt% Ni composite

The electrochemical properties of LaxMg3-xNi9 (x = 1.0-2.0) hydrogen storage alloys

Electrochemical Properties of Cemg11ni+X% Ni Composites (X=0, 50, 100 and 200) Prepared by Ball-Milling

Microstructure and Electrochemical Properties of Mechanically Ground Ce2Mg17 + X Wt.% Ni (x = 0, 50, 100, 200) Composites

Electrode Characteristics of Non-Stoichiometric Ml(Nimnalfe)(X) Alloys

Microstructure and electrochemical properties of amorphous Mg-Fe-Ni hydrogen storage electrode material

Effect of the La/Mg ratio on the structure and electrochemical properties of LaxMg3-xNi9 (x = 1.6 -2.2) hydrogen storage electrode alloys for nickel-metal hydride batteries

The phase structures and electrochemical properties of TiV2.1Nix(x=0.2 similar to 0.6) hydrogen storage alloys

Effect of Co Substitution for Ni on the Structural and Electrochemical Properties of La2Mg(Ni1−xCox)9 (x = 0.1–0.5) Hydrogen Storage Electrode Alloys

Electrode properties of La2Mg17 alloy ball-milled with x wt.% cobalt powder (x = 50, 100, 150 and 200)