Abstract:Amorphous 2Mg–Fe+xwt.% Ni alloys were synthesized by mechanical alloying of Mg and Fe elemental powders. Two kinds of ball-milling atmospheres, namely, (1) under argon and (2) first under argon and then in tetrahydrofuran (THF), were examined in this study. The effects of the Ni addition and ball-milling time and atmosphere on the microstructure and electrochemical properties of the prepared alloys have been investigated systematically. The results show that the ball-milled (2Mg–Fe) nickel-free mixture still maintains Mg and Fe elemental phases, and its discharge capacity is only 19.2mAhg−1. The Ni powder addition is advantageous for the formation of Mg–Fe amorphous structure and for the improvement of the electrochemical properties of the alloys. For the alloys milled under argon, with the Ni content x increasing, the discharge capacity of the alloys increases first and then decreases, and reaches a maximum value of 455.3mAhg−1 as x=100. With the milling-time extending, the discharge capacity of the alloy increases first and then decreases too. For the alloys milled under argon and then in THF, the alloys exhibit higher degree of amorphorization, bigger specific surface area and more active surfaces, and thus have better electrochemical properties than those milled under argon. With the Ni increasing, the discharge capacity increases from 249.7mAhg−1 (x=50) to 565.2mAhg−1 (x=150) and then decreases to 497.9mAhg−1 (x=200), and the exchange current density I0 increases from 104.8mAg−1 (x=50) to 251.1mAg−1 (x=200), which is consistent with the variation of the HRD of the alloy electrodes in the investigation range.

The Electrochemical Evaluation of Ball Milled MgNi-based Hydrogen Storage Alloys

An electrochemical investigation of mechanical alloying of MgNi-based hydrogen storage alloys

Microstructures and electrochemical hydrogen storage properties of novel Mg–Al–Ni amorphous composites

Influence of Ball-milling with Ni Powder on the Phase Structure and Electrochemical Hydrogen Storage Properties of Mg17Al12 Alloy

Mechanical Ball Milling Preparation and Electrochemical Hydrogen Storage Properties of Amorphous Mg-Fe Composites

Microstructure and electrochemical properties of amorphous Mg-Fe-Ni hydrogen storage electrode material

Electrochemical Hydrogen Storage of Ball-Milled Mg-rich Mg–Nd Alloy with Ni Powders

Electrochemical Characteristics of Amorphous Mgtixni (X=0, 0.1, and 0.2) Hydrogen Storage Alloys

The Influence of Ball Milling Process on Formation and Electrochemical Properties of Amorphous MgNi Hydrogen Storage Alloys

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

Effect of the Milling Parameters on the Electrochemical Properties of Milled Amorphous MgNi Hydrogen Storage Alloy

Effect of Ball-Milling Time on the Electrochemical Properties of La–Mg–Ni-based Hydrogen Storage Composite Alloys

Ti–Fe based alloys prepared by ball milling for electrochemical hydrogen storage

Characteristics of Hydride Electrodes Using Mg-Ti-Ni-Co-Al-based Alloys Synthesized by Mechanical Milling

Influence of Ball-Milling with Cu Powder on Electrochemical Properties of V-based Solid Solution Type Hydrogen Storage Alloys

Microstructure and electrochemical properties of amorphous composites of ball-milled Mg2Ni0.95Sn0.05 + x wt% Ni

The Study on the Electrochemical Performance of Mechanically Alloyed MgâTiâNi-based Ternary and Quaternary Hydrogen Storage Electrode Alloys

Effect of ball milling on the structure and electrochemical hydrogen storage properties of a RE-Mg-Ni alloy

Preparation of Mg2Ni Hydrogen Storage Alloy Materials by High Energy Ball Milling

Electrochemical Properties of the Ball-Milled LaMg10Ni2−xAlx Alloys with Ni Powders (x = 0, 0.5, 1 and 1.5)

Preparation of Amorphous Mg-Ni Alloy by Mechanical Alloying and Investigation on Its Hydrogen Storage Properties